Elektrik Akımı Destekli Sinterleme Yöntemi İle Üretilen Stellite 21 Süperalaşımının Sıcak Korozyon Özellikleri
| Autor: | ERGİN, Nuri, ÖZDEMİR, Özkan, ÖZER, Ahmet Yiğit |
|---|---|
| Jazyk: | turečtina |
| Rok vydání: | 2021 |
| Předmět: | |
| Zdroj: | Issue: 28 1185-1189 Avrupa Bilim ve Teknoloji Dergisi |
| ISSN: | 2148-2683 |
| Popis: | In this study, Stellite 21 alloy is produced with a resistance sintering method by using powder obtained from homogeneous mixing with appropriate composition. Then, the sample was exposed to heat treatment in order to improve the properties of the Stellite 21 super alloy such as strength, hardness and its high temperature properties. Microstructure images of the produced material were determined by scanning electron microscope, their phase analyses with x-ray diffraction analysis and elemental analysis methods. Also, corrosion qualities were determined by hot corrosion practices.. Bu çalışmada Stellite 21 süper alaşımı, uygun kompozisyonda hazırlanarak homojen karıştırma sonrası elde edilen toz karışım kullanılmak suretiyle, elektrik akımı destekli sinterleme yöntemi ile üretilmiştir. Daha sonra numunelerin sertlik, mukavemet ve yüksek sıcaklık özellikleri gibi özelliklerini geliştirmek için ısıl işlem uygulanmıştır. Üretilen malzemenin; mikroyapı görüntüleri taramalı elektron mikroskobuyla; faz analizleri, x-ışınları difraksiyon analizi ve elementel analiz incelemesi yöntemiyle belirlenmiştir. Ayrıca korozyon özellikleri sıcak korozyon çalışmaları ile tespit edilmiştir. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|