КОРОЗІЙНА СТІЙКІСТЬ І ТЕПЛОЗАХИСНІ ВЛАСТИВОСТІ КОМПОЗИЦІЙНИХ ПОКРИТТІВ, НАПОВНЕНИХ ЗОЛЬНИМИ МІКРОСФЕРАМИ

Jazyk: ukrajinština
Rok vydání: 2022
Předmět:
Zdroj: Технічні науки та технології; № 1(27) (2022): ТЕХНІЧНІ НАУКИ ТА ТЕХНОЛОГІЇ; 38-44
Technical sciences and technology; No. 1(27) (2022): TECHNICAL SCIENCES AND TECHNOLOGIES; 38-44
Технические науки и технологии; № 1(27) (2022): ТЕХНІЧНІ НАУКИ ТА ТЕХНОЛОГІЇ; 38-44
ISSN: 2411-5363
2519-4569
Popis: Modern branches of chemical production, which are associated with the development of light industry, cosmetology, pharmacy, will require the introduction of new materials and coatings with increased corrosion resistance and thermal protection properties. Possible ways to solve this important scientific and technical problem include finding resource-saving technologies, for which the authors consider the use of promising raw materials to create new composite coatings. These promising materials include ash microspheres of aluminosilicate composition, which are waste from thermal power plantsoperation. The coating is applied by electric arc method on a steel substrate with carbon steel grade A284Gr.D (Cт3) (GOST 380-2005). For their formation, continuously stretched welding wires of ferrite-perlite structure of brand 1066 (65Г) (GOST 14959-79) and low-carbon welding wire of brand ER346 (Св-08) (GOST 2246-70) were used. The aim of the work is the theoretical and experimental studies of corrosion resistance and heat-protective properties of coatings.The corrosion resistance of coatings in naphthalene medium has been experimentally studied: as a result of immersion for 120… 150 days there is a change in color with the formation of an oxide film and an increase in the size of the surface pores by 10… 15%. The results of theoretical calculations of effective coefficients of thermal conductivity and thermal linear expansion for different filling with microspheres are given. The stability of thermophysical properties was experimentally confirmed by studies of heat resistance and thermal stability of coatings sprayed on a steel substrate with carbon steel gradeA284Gr.D (Cт3) (GOST 380-2005), under cyclic loads at temperatures of 570 ℃ / 10 ℃. The obtained results highlight the feasibility of using electric arc coatings with ferrite-perlite structure of brand 1066 (65Г) (GOST 14959-79) and low-carbon welding wire of brand ER346 (Св-08) (GOST 2246-70), filled with ash microspheres of aluminosilicate composition in technologies for protection and restoration of parts and structures of chemical equipment. The scientific significance of the work includes the expansion of ideas about corrosion processes in dispersed metal-matrix coatings dispersed with inorganicmicrospheres and about their maximum resource under conditions of thermocyclic loads.
У статті висвітлено доцільність застосування електродугових покриттів з Св-08 і 65Г, наповнених зольними мікросферами алюмосилікатного складу, в технологіях захисту та відновлення деталей і конструкцій хімічного обладнання. Експериментально досліджено корозійну стійкість покриттів до нафталіну; наведено результати теоретичних розрахунків ефективних коефіцієнтів теплопровідності і термічного лінійного розширення для покриттів зрізним наповненням мікросферами. Стабільність теплофізичних властивостей експериментально підтвердженодослідженнями термостійкості й термостабільності покриттів, напилених на сталеву підкладку з Ст3, в умовах циклічних навантажень при температурах 570 °C/10 °C.