РЕГУЛЮВАННЯ СОРБЦІЙНОЇ ЗДАТНОСТІ КОМБІНОВАНИХ ВОЛОКНИСТИХ МАТЕРІАЛІВ, НАПОВНЕНИХ ГЛИНИСТИМИ МІНЕРАЛАМИ

Jazyk: ukrajinština
Rok vydání: 2022
Předmět:
Zdroj: Технічні науки та технології; № 4(26) (2021): ТЕХНІЧНІ НАУКИ ТА ТЕХНОЛОГІЇ; 113-120
Technical sciences and technology; No. 4(26) (2021): TECHNICAL SCIENCES AND TECHNOLOGIES; 113-120
Технические науки и технологии; № 4(26) (2021): ТЕХНІЧНІ НАУКИ ТА ТЕХНОЛОГІЇ; 113-120
ISSN: 2411-5363
2519-4569
Popis: The results of determining the sorption properties of samples of combined fibrous materials impregnated with dispersions of water-soluble polymers of different types and concentrations filled with clay minerals in relation to the methylene blue dye are presented. The rational composition of dispersions of water-soluble polymers filled with clay minerals is determined. The obtained materials can be used as a reinforcing base of fibrous sorbents for their further use in the treatment of light industry wastewater from dyes and heavy metal ions. The aim of the work is to determine the kinetic regularities of sorption (by methylene blue) of combined fibrous materials impregnated with dispersions of water-soluble polymers of different types and concentrations filled with clay minerals. As a fibrous basis for the composite material used knitted fabric with a surface density of 240 g / m2, which was made of plaited weave using cotton yarn with a linear density of 25 Tex and polyethylene complex threads with a linear density of 16.5 Tex on a single-font circular knitting machine type MS. First, a dispersion of the clay mineral was prepared in an aqueous solution of a polymeric binder, which was then applied with a squeegee knife to the surface of the knitted material. The sorption properties of the samples were determined by the methylene blue dye, the change in optical density was measured on a UNICO 2150 E spectrophotometer, wavelength 600 nm, cuvette 10 mm. Calculated the degree of absorption of the dye from the solution after 24, 48 and 72 hours of treatment. It was determined that increasing the duration of sorption above 48 hours is not rational. The highest degree of absorption of MS is shown by samples of knitted material treated with 3% dispersions of PVA and starch, 78.4 and 77.1%, respectively. This is probably due to the fact that these samples are characterized by the highest content of clay adsorbent, the weight gain for these samples after the introduction of clay adsorbent was 78.7 and 60.1%, respectively. In the case of the use of filled dispersions of CMC and CMS, a larger amount of clay adsorbent is characterized by samples treated with dispersions of CMC and CMC of lower concentration.
Представлені результати визначення сорбційних властивостей зразків комбінованих волокнистих матеріалів, просочених дисперсіями водорозчинних полімерів різних типів і концентрацій, наповнених глинистими мінералами, по відношенню до барвника метиленового синього. Як волокнисту основу для композиційного матеріалу використали трикотажне полотно поверхневою щільністю 240 г/м2. Найвищу ступінь поглинання метиленового синього з розчину демонструють зразки трикотажного матеріалу, оброблені 3%-вими дисперсіями полівінілового спирту і крохмалю. Отримані матеріали можуть використовуватись як зміцнювальна основа волокнистих сорбентів для їх подальшого застосування при очищенні стічних вод легкої промисловості від барвників та іонів важких металів.