Влияние химического состава и структуры на обрабатываемость высокохромистых чугунов
| Autor: | Netrebko, V. V. |
|---|---|
| Jazyk: | ruština |
| Rok vydání: | 2014 |
| Předmět: | |
| Zdroj: | Будівництво, матеріалознавство, машинобудування; № 74 (2014): Будівництво, матеріалознавство, машинобудування; 104-107 Строительство, материаловедение, машиностроение; № 74 (2014): Строительство, материаловедение, машиностроение; 104-107 Construction, materials science, mechanical engineering; № 74 (2014): Construction, materials science, mechanical engineering; 104-107 |
| ISSN: | 2415-7031 |
| Popis: | The influence of carbon and structure on the m achinability of high-chromium cast irons has been studied. With the increase of carbon content in cast iron the machinability becomes worse. When carbon content in cast iron was over 3 % , hypereutectic carbides had been formed, and they worsened the machinability abruptly. Compositions of cast irons for the parts which require mechanical treatment have been recommended. Изучено влияние углерода и структуры на обрабатываемость высокохромисты хчугунов. По мере увеличения содержания углерода в чугуне обрабатываемость ухудшается. При содержании углерода в чугуне свыш е 3% образовывались за эвтектические карбиды , резко ухудшающие обрабатываемость. Реком ендованы составы чугунов для деталей, требующих механической обработки. Вивчено вплив вуглецю та структури на оброблюваність високохромистих чавунів. Як що збільшувати вміст вуглецю в чавуні, то його оброблюваність погіршується. Як що вміст вуглецю в чавуні перевищує 3% то в ньому утворюються заевтектичні карбіди які дуже погіршують його оброблюваність. Запропоновано склад чавунів для деталей, які потребують механічної обробки. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|