Закономірності спучування окисленого графіту в гравітаційно-падаючому шарі
| Autor: | Maslov, V. О., Pustovalov, Y. P., Trofimova, L. О., Dan, L. О. |
|---|---|
| Jazyk: | ukrajinština |
| Rok vydání: | 2020 |
| Předmět: | |
| Zdroj: | Вісник Приазовського Державного Технічного Університету. Серія: Технічні науки; № 40 (2020): Вісник ПДТУ. Серія: Технічні науки; 14-19 Вестник Приазовского государственного технического университета. Серия: Технические науки; № 40 (2020): Вестник ПГТУ. Серия: Технические науки; 14-19 Reporter of the Priazovskyi State Technical University. Section: Technical sciences; № 40 (2020): Reporter of the Priazovskyi State Technical University. Section: Technical sciences; 14-19 |
| ISSN: | 2225-6733 2519-271X |
| Popis: | The final stage of obtaining thermografenite is thermal shock heating of intercalated graphite, which is carried out in a dense moving fluidized layers, in the ascending flow, in the burner flame in the temperature range from 800°С to 1200°С. A fundamentally new approach is the treatment of intercalated graphite in a gravity-falling layer. It makes it possible to carry out the process in a split second. The proposed processing method is based on the principle of independent movement of similar particles. The present paper describes the basic regularities of intercalated graphite thermal expansion in the gravity-falling layer in the furnace temperature field. It has been shown that in the conditions of a gravity-falling layer the intercalated graphite particles almost instantly acquire the temperature of the environment. The research has found out the dependencies of the thermografenite bulk density on the isothermal zone temperature of the furnace have been found in this research. A new technique to study the swelling of oxidized graphite in the gravity-falling layer in the temperature field of the furnace has been proposed. The principle of independent movement of single particles of oxidized graphite has been formulated. It makes it possible to get high heat transfer coefficients (from 1920 to 5760 W/m2∙K) during heating. The main characteristics of the apparatus for producing thermally expanded graphite in the temperature range from 300°C to 1000°C have been proposed and analyzed. Investigation results of the dynamics of the transformation of the intercalated graphite into thermally expanded graphite under different isothermal temperature in a nitrogen atmosphere and the velocity of particles ranging from 0,9 to 0,35 m/s are presented. The obtained results are analyzed in the system of coordinates «bulk density of thermografenite – temperature of the furnace isothermal area». It has been found that the greatest rate of the intercalated graphite expansion is observed in the temperature range from 350 to 600°C anddeeper volumes additional expansion occurs at a higher temperature. Thermografenite with a bulk density from 3 to 5 kg/mhas been obtained in the temperature range from 800 to 1000°C Рассмотрены основные закономерности термического расширения интеркалированного графита в гравитационно-падающем слое в контексте температурного поля печи. Показано, что в условиях гравитационно-падающего слоя частицы интеркалированного графита почти мгновенно приобретают температуру среды. Найдены закономерности, связывающие объемную плотность термографенита с температурой изотермической зоны печи Розглянуті основні закономірності термічного розширення інтеркальованого графіту в шарі, що гравітаційно падає в контексті температурного поля печі. Показано, що в умовах гравітаційно-падаючого шару частинки інтеркальованого графіту майже миттєво набувають температури середовища. Знайдено закономірності, що зв’язують об’ємну щільність термографеніта з температурою ізотермічної зони печі |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|