A facile synthetic route toward air-stable magnetic nanoalloys with Fe-Ni/Fe-Co core and iron oxide shell
| Autor: | Douvalis, A. P., Zboril, R., Bourlinos, A. B., Tucek, J., Spyridi, S., Bakas, T. |
|---|---|
| Rok vydání: | 2012 |
| Předmět: |
Borohydride
ferric hydroxide iron oxide synthesis oxidation Iron Mossbauer spectroscopy magnetic nanoparticle magnetic field reduction Borohydrides Iron oxides Magnetization nickel X ray fluorescence alloy Magnetization measurements Iron alloys Ferrihydrites Ferrihydrite chemical composition Shells (structures) Nanomagnetics degradation Core-shell Molybdenum X ray powder diffraction article Superparamagnetism particle size cobalt Organic solvents priority journal substitution reaction Magnetic fields Synthesis (chemical) Magnetic nanoparticles sodium derivative chemical structure Nanoparticles room temperature Transmission electron microscopy Chemical modification |
| Popis: | Air-stable bimetallic spherically shaped Fe-Ni and Fe-Co magnetic nanoparticles (MNPs), having an average size of 15 nm and core-shell structure, were synthesized by a simple wet chemical method under ambient conditions. For the first time, sodium borohydride reduction method, commonly applied for the syntheses of metal nanoparticles, was used for the preparation of well-defined Fe-Ni and Fe- Co nanoalloys, avoiding exploitation of any organic solvent. This approach allows a large scale production of nanoparticles specifically stabilized by an iron oxyhydroxide shell without a need of secondary functionalization. Transmission electron microscopy, X-ray powder diffraction, X-ray fluorescence, magnetization, and M?ssbauer data demonstrate a core- shell nature of the as-synthesized nanoparticles. The nanoparticle core is of metallic origin and is inhomogeneous at the atomic level, consisting of iron-rich and iron-poor alloy phases. The composition of the shell is close to the ferrihydrite and its role lies in prevention of oxidation-induced degradation of nanoparticle properties. The core is ferromagnetic at and below room temperature, experiencing superparamagnetic relaxation effects due to a reduced size of nanoparticles, whereas the shell is completely superparamagnetic at 300 K and magnetically orders below?25 K. Both developed types of magnetic nanoalloys exhibit a strong magnetic response under applied magnetic fields with a high magnetization values achievable at relatively low applied magnetic fields. Beside this, the highly biocompatible chemical composition of the nanoparticle shell and ability of its chemical modification by substitution or addition of other ions or molecules further empower the application potential of these MNPs, especially in the field of biomedicine. © Springer Science+Business Media B.V. 2012. Journal of Nanoparticle Research |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|