The effect of heat treatment on corrosion behavior of CuAlMn alloy in NaCl solution : diploma thesis
| Autor: | Mađerić, Silvija |
|---|---|
| Přispěvatelé: | Vrsalović, Ladislav |
| Jazyk: | chorvatština |
| Rok vydání: | 2018 |
| Předmět: |
energy disperzive x-ray spectroscopy (EDX)
meausuring the open circuit potenntial potentiodynamic polarization method linear polarization method korozija potenciodinamička polarizacijska metoda TECHNICAL SCIENCES. Chemical Engineering metoda energetski disperzivne rendgenske spektroskopije(EDX) kloridni ioni pretražna elektronska mikroskopija (SEM) copper alloys CuAlMn legura corrosion toplinska obrada heat treatment TEHNIČKE ZNANOSTI. Kemijsko inženjerstvo legure bakra mjerenje potencijala otvorenog strujnog kruga SEM/EDS analysis CuAlMn alloy smart materials SEM/EDS analiza chloride ions elektrokemijske metode pametni materijali legure s prisjetljivosti oblika (SMA) shape memory alloys(SMA) electrochemical metods metoda linearne polarizacije |
| Popis: | Utjecaj toplinske obrade legure CuAlMn na korozijsko ponašanje u 0,1 %, 0,9 % i 1,5 % otopini NaCl ispitan je elektrokemijskim metodama kao što su mjerenje potencijala otvorenog strujnog kruga, metodom linearne i potenciodinamičke polarizacije. Nakon polarizacijskih mjerenja elektrodna površina je ispitana optičkim mikroskopom te je provedena i SEM/EDS analiza. Rezultati ispitivanja su pokazali da toplinski obrađeni uzorci pokazuju nešto pozitivniju vrijednost potencijala u odnosu na lijevani uzorak. Povećanjem koncentracije kloridnih iona dolazi do stabilizacije potencijala pri nešto negativnijim vrijednostima za sve ispitivane uzorke CuAlMn. Gustoća korozijske struje nešto je manja, a polarizacijski otpor veći za toplinski obrađene uzorke u odnosu na uzorak lijevane legure bez toplinske obrade. Na mikroskopskim snimkama površine nakon polarizacijskih mjerenja se može vidjeti hrapava površina elektroda uslijed odvijanja korozijskih procesa. Povećanje koncentracije elektrolita dovodi do povećanja oštećenja površine elektroda. Ispitivanja pretražnom elektronskom mikroskopijom pokazala su da je površina prekrivena isprekidanim slojevima korozijskih produkata, kao i pukotinama i kanalićima koji su nastali njihovim otapanjem. Elementarna analiza površine metodom energetski disperzivne rendgenske spektroskopije pokazala je da se korozijski produkti sastoje od aluminijeva i manganova oksida i klorida čiji se postotak razlikuje u ovisnosti od mjesta na kojoj je provedena analiza. Značajno manji sadržaj bakra na površini nađen je na površini kaljenog uzorka CuAlMn legure u odnosu na površinu uzorka lijevane CuAlMn legure bez toplinske obrade. The influence of heat treatment of CuAlMn alloy on corrosion behavior in 0.1%, 0.9% and 1.5% NaCl solution was studied by electrochemical methods such as measuring the open circuit potential, linear and potentiodynamic polarization. After polarization measurements the electrode surfaces was examined by optical microscope and also with SEM/EDS analysis. The results of the investigations have shown that the heat treated samples have a slightly more positive values of the open circuit potential compared to the as cast sample. Concentration increasing of chloride ions results in potential stabilization at slightly negative values for all CuAlMn alloy samples. Values of the corrosion current density are slightly smaller and the polarization resistance values are higher for the heat treated samples compared to the sample of as cast alloy without heat treatment. The microscopic analysis of the electrode surfaces after the polarization measurements, have show the rough surfaces due to corrosion processes. Increasing the electrolyte concentration leads to an increase in electrode surface damage. Examination by scanning electron microscopy showed that the surface was covered with interlaced layers of corrosion products, as well as cracks and ducts formed by their dissolution. Elemental surface analysis by energy dispersive X-ray spectroscopy showed that corrosive products consist of aluminum and manganese oxides and chlorides, the percentage of which differs depending on the site where the analysis was performed. Significantly lower copper content on the surface was found on the surface of the annealing CuAlMn alloy sample surface relative to the surface of the cast CuAlMn alloy without heat treatment. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|