Investigation of corrosion behavior of CuAlMnTi alloy ribons made by rapid solidification in 0.9% NaCl solution : bachelor thesis
| Autor: | Jerčić, Radosna |
|---|---|
| Přispěvatelé: | Vrsalović, Ladislav |
| Jazyk: | chorvatština |
| Rok vydání: | 2018 |
| Předmět: |
corrosion
TEHNIČKE ZNANOSTI. Kemijsko inženjerstvo legure bakra meausuring the open circuit potenntial potentiodynamic polarization method linear polarization method CuAlMnTi alloy mjerenje potencijala otvorenog strujnog kruga korozija CuAlMnTi legura SEM/EDS analysis potenciodinamička polarizacijska metoda TECHNICAL SCIENCES. Chemical Engineering smart materials SEM/EDS analiza chloride ions kloridni ioni elektrokemijske metode pametni materijali legure s prisjetljivosti oblika (SMA) shape memory alloys(SMA) copper alloys electrochemical metods metoda linearne polarizacije |
| Popis: | Korozijsko ponašanje CuAlMnTi traka dobivenih brzim hlađenjem ispitano je u 0,9% NaCl otopini pri temperaturama10, 24, 37 i 50 o C. Također je ispitan i utjecaj pH vrijednost elektrolita na koroziju traka CuAlMnTi legure u 0,9 % NaCl otopini pH vrijednosti 3,4, 5,4 i 7,4. Mjerenja su provedena elektrokemijskim metodama kao što su praćenje potencijala otvorenog strujnog kruga, metodama linearne i potenciodinamičke polarizacije. Rezultati ispitivanja su pokazali da povećanje temperature elektrolita i sniženje pH vrijednosti dovodi do negativiranja vrijednosti korozijskog potencijala, porasta gustoće korozijske struje i smanjenja vrijednosti polarizacijskog otpora što ukazuje na veći korozijski napad na CuAlMnTi leguru. Na snimkama površine koje su dobivene svjetlosnim mikroskopom vidljiva su oštećenja površine uslijed korozijskog procesa, koja se povećavaju s povišenjem temperature elektrolita i sniženjem pH vrijednosti otopine. Jamičasta korozija vidljiva je nakon polarizacijskog ispitivanja pri 50 o C. SEM snimke su potvrdile negativan utjecaj povišenja temperature i sniženja pH vrijednosti elektrolita na koroziju CuAlMnTi legure. EDS analizom utvrđena je prisutnost svih legirnih elemenata na površini, ali se njihov postotak smanjuje osobito sniženjem pH vrijednosti elektrolita. Bakar i aluminij se najprije otapaju s površine a zatim mangan, dok se postotak Ti značajnije ne mijenja uslijed korozijskih procesa što potvrđuje njegovu izrazitu korozijsku otpornost. The corrosion behavior of CuAlMnTi alloy ribbons obtained by rapid cooling was assayed in 0.9% NaCl solution at temperatures of 10, 24, 37 and 50 o C. The influence of different pH value of electrolyte on corrosion of CuAlMnTi alloy ribbons in 0.9% NaCl (pH = 3.4, 5.4 and 7.4) was also investigated. Measurements were performed by electrochemical methods such as monitoring the open circuit current potential, linear and potentiodynamic polarization methods. The results of the measurements have shown that the increase in temperature of the electrolyte and the decrease of pH value leads to a change of corrosion potential values in negative direction, a rise in corrosion current density values, and a decrease in polarization resistance values, indicating a higher corrosion attack on CuAlMnTi alloy. Surface images obtained by a light microscope show surface damages due to the corrosion process, which are increased by elevation of the electrolyte temperature and by lowering the pH of the solution. Pitting corrosion is visible after a polarization test at 50 o C. Results of SEM investigations confirmed the negative influence of temperature elevation and lower electrolyte pH on CuAlMnTi alloy corrosion. By EDS analysis, the presence of all alloying elements on the surface was determined, but their percentage decreased, especially by lowering the pH of the electrolyte. Copper and aluminum first dissolve from the surface and then manganese, whereas the percentage does not significantly change due to corrosion processes, which confirms its marked corrosion resistance. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|