Investigation of corrosion behavior of CuAlNi alloy ribons made by rapid solidification in NaCl solution : bachelor thesis
| Autor: | Garvanović, Ines |
|---|---|
| Přispěvatelé: | Vrsalović, Ladislav |
| Jazyk: | chorvatština |
| Rok vydání: | 2018 |
| Předmět: |
corrosion
legure s prisjetljivosti oblika TEHNIČKE ZNANOSTI. Kemijsko inženjerstvo legure bakra CuAlNi alloys korozija SEM/EDS analysis TECHNICAL SCIENCES. Chemical Engineering smart materials SEM/EDS analiza elektrokemijske metode pametni materijali CuAlNi legura shape memory alloys(SMA) electrochemical metods |
| Popis: | Korozijsko ponašanje CuAlNi traka dobivenih naglim hlađenjem ispitano je u 0,9 % NaCl otopini (pH = 7,4) pri temperaturama 24, 37 i 50 o C. Također je ispitan i utjecaj koncentracije kloridnih iona na koroziju traka Cu-Al-Ni u 0,1 % i 1,5 % otopini NaCl. Mjerenja su provedena elektrokemijskim metodama kao što su praćenje potencijala otvorenog strujnog kruga, metodama linearne i potenciodinamičke polarizacije. Rezultati ispitivanja su pokazali da povećanje koncentracije kloridnih iona i temperature elektrolita dovodi do porasta gustoće korozijske struje i smanjenja vrijednosti polarizacijskog otpora što ukazuje na veći korozijski napad na CuAlNi leguru. Mikroskopske snimke su ukazale na značajna oštećenja na površini CuAlNi legure uzrokovana jamičastom korozijom. SEM snimke površine CuAlNi elektroda su potvrdile da s povećanjem koncentracije kloridnih iona dolazi do većeg korozijskog napada. EDS analiza ukazala je na dominantan postotak bakra, klora i kisika na površini što ukazuje na formiranje bakrovih oksida i klorida kao glavnih produkata korozije na površini. Mali postotak aluminija ukazuje na njegovu raspodjelu u obliku aluminijeva oksida i klorida u površinskom sloju. The corrosion behavior of the CuAlNi alloy ribbons obtained by rapid solidification was investigated in 0.9 % NaCl solution (pH 7.4) at temperatures of 24, 37 and 50 o C. The influence of chloride ions concentration on corrosion of CuAlNi ribbons has also been investigated in 0.1% and 1.5% NaCl solution. Measurements have been performed by electrochemical methods such as monitoring the open circuit potential, linear and potentiodynamic polarization methods. Results of the investigations have shown that increase in chloride concentration and electrolyte temperature leads to increase the corrosion current density and decrease the polarization resistance values which mean higher corrosion attack on CuAlNi alloy. Microscopic images have shown significant pitting corrosion damages on the CuAlNi alloy surface. Increasing the electrolyte temperature increases the surface damages of the electrode due to more intense corrosion. SEM surface images of CuAlNi electrodes have confirmed that with elevation of chloride concentration a more intense corrosion attack occurs. EDS surface analysis indicated dominant percentage of copper, chlorine and oxygen on the surface, indicating the formation of copper oxide and chloride as the major corrosion products on the surface. The presence of a small percentage of aluminum indicates its distribution in the form of aluminum oxide and chloride in the surface layer. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|