| Autor: |
Kociubczyk, Alex Iván, Cabello, Federico, Schvezov, Carlos Enrique, Gregorutti, Ricardo Walter, Ares, Alicia Esther |
| Jazyk: |
angličtina |
| Rok vydání: |
2014 |
| Předmět: |
|
| DOI: |
10.1002/9781118888438.ch181/summary |
| Popis: |
Al-Cu eutectic alloy samples (Al-33.2wt.%Cu) were solidified directionally upward under conditions which produce the columnar-to-equiaxed transition (CET) phenomenon. The position of the CET was located in each sample and the distance from the bottom of the ingot was measured. During solidification the distribution of temperatures were measured by means of thermocouples located strategically. From the measured temperatures the following parameters were obtained; local temperature gradient, cooling rate of the liquid and solid and growth rate. Three different velocities of heat extraction were employed and the temperature gradient reaches values of 2.1 ºC/cm, 0.1 °C/cm and -4.3ºC/cm, respectively. The results are presented and discussed comparing with the results obtained in the case of CET in dendritic Al-Cu alloys Fil: Kociubczyk, Alex Iván. Consejo Nacional de Investigaciones Cientificas y Tecnicas. Centro Cientifico Tecnológico Nordeste. Instituto de Materiales de Misiones; Argentina Fil: Cabello, Federico. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina Fil: Schvezov, Carlos Enrique. Consejo Nacional de Investigaciones Cientificas y Tecnicas. Centro Cientifico Tecnológico Nordeste. Instituto de Materiales de Misiones; Argentina Fil: Gregorutti, Ricardo Walter. Universidad Nacional de La Plata; Argentina Fil: Ares, Alicia Esther. Consejo Nacional de Investigaciones Cientificas y Tecnicas. Centro Cientifico Tecnológico Nordeste. Instituto de Materiales de Misiones; Argentina |
| Databáze: |
OpenAIRE |
| Externí odkaz: |
|