Mineral carbonation of construction and demolition waste is a viable alternative for the reduction of CO2 emissions from industry. Concrete and cement, together with ceramic blocks, are the primary sources of calcium for mineral carbonation in which CO2 is fixed in a stable and inert process. One type of concrete was selected from 5 for the carbonation tests. Crushed, separated into size fractions, moistened to 20% and tested at 10 bars of CO2 for 24 to 720h. Destruction of portlandite and ettringite phases was determined. Calcite precipitated as carbonate phase. Maximum carbonation was reached after 72h, fixing 6.5% of CO2. La carbonatación mineral de los residuos de construcción y demolición es una alternativa viable para la reducción de las emisiones de CO2 de la industria. El hormigón y el cemento, junto con los bloques de cerámica, son las principales fuentes de calcio para la carbonatación mineral en la que el CO2 se fija en un proceso estable e inerte. Se seleccionó un tipo de hormigón de entre 5 para las pruebas de carbonatación. Triturado, separado en fracciones de tamano, ˜ humedecido al 20% y probado a 10 bares de CO2 durante 24 a 720 horas. Se determinó la destrucción de las fases de portlanita y ettringita. La calcita se precipitó como fase de carbonato. La máxima carbonatación se alcanzó después de 72 horas, fijando el 6,5% de CO2. Junta de Andalucía P12-RNM-568 |
| Databáze: |
OpenAIRE |
| Externí odkaz: |
|