| Autor: |
Nenastina, T. A., Ved, M. V., Sakhnenko, N. D., Proskurina, V. O., Fomina, L. P. |
| Jazyk: |
angličtina |
| Rok vydání: |
2020 |
| Předmět: |
|
| Popis: |
The functional properties of ternary Co-W-Zr(ZrO₂) alloys obtained in a pulsed mode from pyrophosphate-citrate electrolytes are discussed. The obtained coatings are characterized by a uniformly developed surface without cracks and a sufficiently high and reproducible microhardness. It was determined that the size of the globules on the alloy surface decreases with increasing of the current density to 10 A/dm². It was found that increase of temperature favorably affects the current efficiency of the alloy and the microhardness of the Co-W-Zr(ZrO₂) coating. The modes of electrosynthesis of the coatings by cobalt-tungsten-zirconium alloys are substantiated, an their influence on the functional properties of the alloy and current efficiency is investigated. Обговорено функціональні властивості потрійних сплавів Co-W-Zr(ZrO₂), отриманих в імпульсному режимі з пірофосфатно-цитратних електролітів. Отримані покриття характеризуються рівномірно розвиненою поверхнею без тріщин і достатньо високою відтворюваною мікротвердістю. Встановлено, що розмір глобул на поверхні сплаву зменшується зі збільшенням густини струму до 10 А/дм². Встановлено, що підвищення температури сприятливо впливає на вихід по струму сплаву та мікротвердість покриття Co-W-Zr(ZrO₂). Обґрунтовано режими електросинтезу покриттів кобальтовольфрамоцирконієвими сплавами, досліджено їх вплив на функціональні властивості сплаву та вихід по струму. |
| Databáze: |
OpenAIRE |
| Externí odkaz: |
|