| Popis: |
Ultra‐thin Cu(In,Ga)Se2(CIGS) solar cells with an Al2O3rear surface passivation layer between the rear contact and absorber layer frequently show a “roll‐over” effect in theJ–Vcurve, lowering the open circuit voltage (VOC), short circuit current (JSC) and fill factor (FF), similar to what is observed for Na‐deficient devices. Since Al2O3is a well‐known barrier for Na, this behaviour can indeed be interpreted as due to lack of Na in the CIGS absorber layer. In this work, applying an electric field between the backside of the soda lime glass (SLG) substrate and the SLG/rear‐contact interface is investi‐gated as potential treatment for such Na‐deficient rear surface passivated CIGS solar cells. First, an electrical field of +50 V is applied at 85 °C, which increases the Na concentration in the CIGS absorber layer and the CdS buffer layer as measured by glow discharge optical emission spectroscopy (GDOES). Subsequently, the field polarity is reversed and part of the previously added Na is removed. This way, theJ–Vcurve roll‐over related to Na deficiency disappears and theVOC(+25 mV),JSC(+2.3 mA/cm2) and FF (+13.5% absolute) of the rear surface passivated CIGS solar cells are optimized. |