Aluminous binding materials based on the slag of aluminothermal production of ferrotitanium and cell concrete on their basis
| Autor: | Abyzov, V. A., Chernogorlov, S. N. |
|---|---|
| Rok vydání: | 2015 |
| Předmět: |
calcium aluminate hydrate
огнеупорность fire resistance УДК 666.948.4 шлак ферротитана heat-resistance cell concrete modified aluminous binding aluminous cement slag of aluminothermal production гидроалюминаты кальция глиноземистый цемент УДК 666.974.2 high-alumina cement ГРНТИ 67.09 суперпластификатор на основе эфиров поликарбоксилатов slag of ferrotitanium шлак алюминотермического производства hydration of calcium aluminate высокоглиноземистый цемент модифицированное глиноземистое вяжущее superplasticizing admixtures based on polycarboxylic ether УДК 691.327.332 жаростойкий ячеистый бетон гидратация алюминатов кальция heat-resistant properties жаростойкие свойства |
| Popis: | На основе глиноземистого цемента, шлака алюминотермической выплавки ферротитана и добавок суперпластификаторов на основе эфиров поликарбоксилатов (РСЕ) разработано модифицированное глиноземистое вяжущее. Изучены методами физико-химического анализа особенности гидратации вяжущего в присутствии данных добавок. Показано, что в начальные сроки твердения (3–7 сут) скорость гидратации алюминатов кальция в различной степени снижается под действием суперпластификаторов на основе РСЕ. Выявлены добавки, в наименьшей степени замедляющие твердение, установлены их оптимальные дозировки. Исследовано влияние данных добавок на свойства вяжущего. Получено модифицированное вяжущее с повышенной огнеупорностью (1520–1550 °С). Показано, что применение суперпластификаторов на основе РСЕ обеспечивает вяжущему, содержащему шлак алюминотермической выплавки ферротитана, высокие прочностные показатели. На основе разработанного вяжущего, шамотного и огнеупорного заполнителя получены жаростойкие ячеистые бетоны с температурой применения до 1300 °С. The modified aluminous binding material is developed on the basis of aluminous cement, slag of aluminothermal output of ferrotitanium and superplasticizing admixtures based on polycarboxylic ether. The peculiarities of hydration of binding materials in the presence of these additives are examined by the methods of physical and chemical analysis. It’s shown that at the initial stages of hardening (3–7 days) the speed of hydration of calcium aluminates to different extents is reduced under the influence of superplasticizing admixtures based on polycarboxylic ether. The additives which at least slow down hardening are revealed, their optimal doses are specified. The influence of these additives on a binding property is examined. The modified binding material with increased fire resistance (1520–1550 С) is obtained. It’s shown that the use of superplasticizing admixtures based on polycarboxylic ether provides the binding material, which contains the slag of aluminothermal output of ferrotitanium, with high strength properties. The heat-resistance cell concrete with the operating temperature up to 1300С is produced on the basis of the developed binding material, fire clay and fireproof aggregates. Абызов Виктор Александрович, доцент, кандидат технических наук, доцент кафедры «Строительные материалы», Южно-Уральский государственный университет (Челябинск), uralniist@mail.ru Черногорлов Сергей Николаевич, аспирант кафедры «Строительные материалы», Южно-Уральский государственный университет (Челябинск), gerimoand2@mail.ru. V.A. Abyzov, South Ural State University, Chelyabinsk, Russian Federation, uralniist@mail.ru S.N. Chernogorlov, South Ural State University, Chelyabinsk, Russian Federation, gerimoand2@mail.ru |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|