Sinteza fenolne smole ojačane nanočesticama TiO2 i njezin utjecaj na gorivost lamelirane drvne građe (LVL)

Autor: Özbay, Günay, Atar, Musa, Ozcifci, Ayhan
Jazyk: angličtina
Rok vydání: 2023
Předmět:
Zdroj: Drvna industrija
Volume 74
Issue 1
ISSN: 1847-1153
0012-6772
Popis: In this study, phenol-formaldehyde (PF) resin has been modified with titanium dioxide nanoparticles (nano-TiO2) at a varying ratio from 0.05 wt.% to 1.5 wt.% to enhance the thermal properties and combustion performance of the resins. The effect of the nano-TiO2 modification on the properties (chemical or thermal) of the resins was determined by Fourier to transform infrared (FT-IR) and thermal analysis (TGA) techniques. In addition, the combustion performance of laminated veneer lumber (LVL) samples bonded with the PF resin modified with nano-TiO2 was tested. The result of the FT-IR analysis indicated that the modified PF resins had match peaks to the reference PF resin. These similarities of the peaks supported that the modified PF resins were successfully synthesise with phenol, formaldehyde, and nano-TiO2. The PF resins modified by nano-TiO2 demonstrated better thermal stability than the reference resin. The nano-TiO2 modified PF resin exhibited a favourable influence on the combustion characteristics of LVL. In consequence, PF resin modified with nano-TiO2 could be used as a combustion retardant adhesive in the wood industry.
U ovom je istraživanju fenol-formaldehidna smola (PF) modificirana nanočesticama titanijeva dioksida (nano-TiO2) u različitim omjerima, od 0,05 tež.% do 1,5 tež.% kako bi se poboljšala njezina toplinska svojstva i svojstva gorivosti. Utjecaj modifikacije nanočesticama TiO2 na svojstva smola (kemijska i toplinska) određen je Fourierovom transformiranom infracrvenom spektroskopijom (FT-IR) i termogravimetrijskom analizom (TGA). Osim toga, ispitana je gorivost uzoraka lamelirane drvne građe (LVL) lijepljene PF smolom modificiranom nano-česticama TiO2. Rezultati FT-IR analize pokazali su da modificirane PF smole imaju jednake vrhove kao referentna PF smola. Te sličnosti vrhova potvrđuju da su modificirane PF smole uspješno sintetizirane s fenolom, formaldehidom i nanočesticama TiO2. PF smole modificirane nanočesticama TiO2 pokazale su bolju toplinsku stabilnost od referentne smole i povoljno su utjecale na gorivost LVL-a. Stoga zaključujemo da bi se PF smola modificirana nanočesticama TiO2 mogla upotrebljavati kao ljepilo za usporavanje gorenja u drvnoj industriji.
Databáze: OpenAIRE
Externí odkaz: