Increasing of hot workability of 1.3302HIGH speed steel
| Autor: | D. Bombač, M. Terčelj, M. Fazarinc, P. Fajfar |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2012 |
| Předmět: | |
| Zdroj: | Metalurgija Volume 51 Issue 3 |
| ISSN: | 1334-2576 0543-5846 |
| Popis: | Laboratory investigation of hot workability of 1.3302 high speed steel was carried out and its improving was achieved. Hot compression tests for the determination of optimal soaking temperature as well as for the study of hot workability in temperature range 1150-850 ºC, strain rates range 0,001-6 s–1 and applied strain up to 0,9 were performed. Microstructure of deformed specimen was analyzed. Apparent activation energies for hot working for upper and for lower temperature range were calculated. Onsets of dynamical recrystallization for applied deformation conditions on the basis of calculated strain hardening ratewere determined. Extending of hot working temperature range at its lower limit, i.e. down to 850 ºC, by applying optimal soaking temperature was obtained. Data su laboratorijska istraživanja prerađivačkih svojstva brzoreznog čelika 1.3302 u vrućem stanju koji su doprinijeli poboljšanju tih svojstava. Izvedeni su pokusi vrućeg sabijanja za određivanje temperature zagrijavanja kao i prerađivačkih svojstva u temperaturnom rasponu 1 150-850 ºC, brzinom deformacije 0,001-6 s–1 i stupnja deformacije do 0,9. Analizirana je mikrostruktura deformiranih proba.Izračunane su prividne aktivacijske energije za vruću preradu za gornje i donje temperaturno područje. Počeci dinamičke rekristalizacije za primijenjene uvjete deformacije utvrđeni su na temelju izračuna brzine deformacijskog očvršćavanja. Primjenjujući optimalno temperaturu zagrijavanja dobiveno je povećanje vrućeg radnog temperaturnog raspona na svojoj donjoj granici, odnosno do 850 ºC. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|