Die Verwendung vom Lichtbogenofenstaub in der Behandlung vom Prozessabwasser aus der Verzinkerei
| Autor: | Višnja Oreščanin, Loris Ezel, Tahir Soflić |
|---|---|
| Jazyk: | chorvatština |
| Rok vydání: | 2020 |
| Předmět: |
elektropećna prašina
alkalna ekstrakcija alkalni kruti ostatak otpadne vode od pocinčavanja cink otpadni mulj electric arc furnace dust alkaline extraction alkaline solid residue wastewater from the galvanising process zinc sludge Lichtbogenofenstaub alkalische Extraktion alkalischer fester Rückstand Prozessabwasser aus der Verzinkerei Zink Abfallschlamm |
| Zdroj: | Hrvatske vode Volume 28 Issue 112 |
| ISSN: | 1849-0506 1330-1144 |
| Popis: | Cilj ovog rada je izdvajanje cinka iz elektropećne prašine postupkom alkalne ekstrakcije pomoću jake natrijeve lužine te korištenje visokog neutralizacijskog/koagulacijskog učinka preostalog alkalnog krutog ostatka za obradu kiselih industrijskih otpadnih voda. Ispitana je i mogućnost regeneracije otpadnog mulja postupkom alkalne ekstrakcije cinka te primjene preostalog krutog ostatka za obradu kiselih otpadnih voda. U tu svrhu je korišteno sedam kompozitnih uzoraka elektropećne prašine iz Siskačke čeličane s udjelom cinka u rasponu od 5,71% do 28,18%. Alkalnom ekstrakcijom izdvojeno je između 62,4 i 84,6% cinka a sastav eluata preostalog krutog ostatka je zadovoljavao uvjete za odlaganje na odlagalište inertnog otpada. Njegovom primjenom za obradu otpadnih voda od pocinčavanja pri optimalnim uvjetima (pH = 8; tkon. = 20 min.) je uklonjeno između 99,17% i 100% teških metala čime su postignute vrijednosti koncentracija elemenata pogodne za ispust u okoliš. Otpadni mulj je regeneriran izdvajanjem cinka postupkom alkalne ekstrakcije a preostali kruti ostatak ponovo uspješno primjenjen za pročiščavanje kiselih otpadnih voda sa sličnom učinkovitosti uklanjanja kao i u prethodnom eksperimentu. The objective of our work was to isolate zinc from electric arc furnace dust using the procedure of alkaline extraction with strong sodium hydroxide base and high neutralization/coagulation effect of the remaining alkaline solid residue for treating acidic industrial wastewater. The possibility of sludge regeneration was also tested using the procedure of alkaline zinc extraction and the application of the remaining solid residue for treating acidic wastewater. To this end, seven samples of composite electric arc furnace dust from the Sisak steel mill with zinc content ranging from 5.71% to 28.18% were used. By means of alkaline extraction, between 62.4 and 84.6% zinc was isolated. The composition of eluate from the remaining solid residue met the criteria for disposal at inert waste disposal sites. Its use in treating wastewater from the galvanizing process in optimal conditions (pH = 8; tcon = 20 min.) removed between 99.17% and 100% of heavy metals, thus achieving the concentration values of elements suitable for discharge into the environment. The sludge was regenerated by zinc isolation using alkaline extraction while the remaining solid residue was successfully reused for treating acidic wastewater with a similar removal efficiency as in the previous experiment. Das Ziel dieser Arbeit ist Extraktion von Zink aus dem Lichtbogenofenstaub durch alkalische Extraktion mit einer starken Base NaOH und die Verwendung der starken neutralisierenden Wirkung und Koagulationswirkung des alkalischen festen Rückstands in der Behandlung von sauren Industrieabwässern. Außerdem wurden die Möglichkeit der Regeneration des Abfallschlammes im Verfahren der alkalischen Extraktion von Zink und die Möglichkeit der Verwendung des festen Rückstands in der Behandlung von sauren Abwässern geprüft. Zu diesem Zwecke wurden sieben Verbundwerkstoffproben vom Lichtbogenofenstaub mit dem Zinkanteil zwischen 5,71% und 28,18% aus dem Stahlwerk Sisak verwendet. Durch alkalische Extraktion wurde zwischen 62,4 und 84,6% Zink extrahiert, und die Zusammensetzung des Eluats befriedigte die Bedingungen für die Entsorgung auf einer Inertabfalldeponie. Durch die Anwendung der alkalischen Extraktion in der Behandlung vom Prozessabwasser aus der Verzinkerei unter optimalen Bedingungen (pH = 8; Kontaktzeit = 20 min) wurden zwischen 99,17% und 100% Schwermetalle beseitigt, womit die Konzentrationswerte von Elementen erzielt wurden, die Freisetzung in die Umwelt erlauben. Der Abfallschlamm wurde durch die alkalische Extraktion von Zink regeneriert, und der feste Rückstand wurde wieder in der Behandlung von sauren Abwässern mit einer ähnlichen Wirksamkeit wie in der ersten Untersuchung verwendet. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|