INVESTIGATION ELECTRO — SPARK DEPOSITS AFTER JOULE HEATING
| Autor: | Trekin, G. E., Shevchenko, O. I. |
|---|---|
| Jazyk: | ruština |
| Rok vydání: | 2020 |
| Předmět: |
METALLOGRAPHIC INVESTIGATION
МИКРОСТРУКТУРА MICROSTRUCTURE INVESTIGATION МЕТАЛЛОГРАФИЧЕСКОЕ ИССЛЕДОВАНИЕ ВЫСОКОТЕМПЕРАТУРНЫЙ НАГРЕВ МИКРОСТРУКТУРА ПОКРЫТИЙ ЭЛЕКТРОИСКРОВОЕ ЛЕГИРОВАНИЕ ИССЛЕДОВАНИЕ МИКРОСТРУКТУРЫ COATINGS MICROSTRUCTURE ALUMINUM ELECTRO-SPARK DEPOSIT HIGH-TEMPERATURE HEATING ELECTRO-SPARK ALLOYING MICROSTRUCTURE ЭЛЕКТРОИСКРОВОЕ ЛЕГИРОВАНИЕ АЛЮМИНИЕМ И ТИТАНОМ TITANIUM ELECTRO-SPARK DEPOSIT |
| Popis: | In this article the influence high — temperature Joule heating on microstructure aluminum and titanium electro-spark deposits was considered. Electro-spark procedure was carried on conventional parameters by means of rotating electrode atop surfaces sheet — samples of low carbon steel in air environment. Was fixed, that after electro-spark alloying by means of both electrodes formed hard deposits. For aluminum deposit, high — temperature heating perform it to whit more thick layer with low micro-hardness. In place former titanium deposit was appeared local small volumes of melting with dendrite structure and middle micro-hardness. В статье рассмотрено влияние высокотемпературного нагрева проходящим током на структуру электроискровых покрытий из алюминия и титана, нанесенных в воздушной среде на низкоуглеродистую сталь вращающимся электродом на типовых режимах. Установлено, что после электроискрового легирования обоими электродами формируется твердый слой. Для алюминиевого покрытия после высокотемпературного нагрева и охлаждения образуется более толстый белый слой с микротвердостью на уровне основного металла. На месте титанового покрытия выявляются участки плавления, более твердые по сравнению с основным металлом и имеющие дендритную структуру. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|