FIELD: physical chemistry. SUBSTANCE: invention relates to the production of zinc powder from zinc-containing raw materials. The method involves the electrochemical reduction of zinc from a zinc-containing compound in an alkaline electrolyte. Zinc oxide is used as a zinc-containing compound, the electrochemical reduction is carried out by direct contact of the solid phase of zinc oxide with the cathode, while the cathode current density is 4000-5000 A/m2, and the alkali content in the electrolyte during the electrolysis is maintained in the range of 30-70 g/l. To increase the speed of the process, 5-10% of the zinc powder by weight of the zinc oxide is added to the zinc oxide before electrolysis. EFFECT: method makes it possible to increase the specific rate of zinc reduction and to obtain a fine powder. 1 cl, 1 dwg. Изобретение относится к получению цинкового порошка из цинксодержащего сырья. Способ включает электрохимическое восстановление цинка из цинксодержащего соединения в щелочном электролите. В качестве цинксодержащего соединения используют оксид цинка, электрохимическое восстановление проводят при непосредственном контактировании твердой фазы оксида цинка с катодом, при этом катодная плотность тока составляет 4000 - 5000 А/м2, а содержание щелочи в электролите по ходу электролиза поддерживают в диапазоне 30-70 г/л. Для повышения скорости процесса перед электролизом в оксид цинка добавляют 5-10% цинкового порошка от массы оксида цинка. Способ позволяет повысить удельную скорость восстановления цинка и получить тонкодисперсный порошок. 1 ил. |
| Databáze: |
OpenAIRE |
| Externí odkaz: |
|