RELATION BETWEEN STRUCTURE AND PROPERTIES FOR A SECTION OF LARGE-SIZE BILLET FROM TITANIUM ALLOY PT‑7M

Autor: Vodolazskiy, F. V., Illarionova, S. M., Barannikova, N. A., Gornostaeva, E. A., Kosmatskiy, Ya. I., Illarionov, A. G.
Jazyk: ruština
Rok vydání: 2018
Předmět:
Popis: In the work of making macro-, micro-, X‑ray structural analyzes, durometry and hot upsetting operation at 875 °C, changes in the structure, hardness and hot strength over the cross section of a hot-baked titanium alloy PT‑7M were studied. It was established that the macrostructure of the microstructure over the cross section of the investigated billet of alloy PT‑7M is characterized by a decrease in the proportion of large macrogranes and recrystallized grains from the center to the surface of the semi-finished product. This contributes to the growth of hardness, the real stresses duaring compression test at 875 °C with increasing distance from the center of the billet. В работе методами макро-, микро-, рентгеноструктурного анализов, дюрометрии и испытаний на горячую осадку при 875 °C изучено изменение структуры, твердости и горячей прочности по сечению горячекованной заготовки из титанового сплава ПТ‑7М. Установлено, что для макро-, микроструктуры по сечению исследованной заготовки из сплава ПТ‑7М характерно уменьшение доли крупных макрозерен и рекристаллизованных зерен от центра к поверхности полуфабриката. Это способствует росту твердости, истинных напряжений при испытаниях на сжатие при 875 °C по мере удаления от центра заготовки. Исследование выполнено за счет гранта Российского научного фонда (проект № 18-79-10107).
Databáze: OpenAIRE