Revista IBRACON de Estruturas e Materiais, Volume: 5, Issue: 6, Pages: 798-811, Published: DEC 2012 |
| Popis: |
The Brazilian standard NBR 7212 states that the time of transporting the concrete between the start of mixing should be less than 90 minutes so that by the end of the discharge is a maximum of 150 minutes. Yet often, in construction, concrete is used after this period. In order to investigate the behavior of concrete after setting time of cement was cast six concrete mixtures with two types of cement. The mixtures were produced and kept fresh for six hours, adopting a procedure for maintenance of abatement by superplasticizer and agitation. The results show that of the test piece molded over six hours of maintained or increased the compressive strength average. A norma brasileira NBR 7212 coloca que o tempo de transporte do concreto decorrido entre o início da mistura deve ser inferior a 90 minutos de maneira que até o fim da descarga seja de no máximo 150 minutos. No entanto muitas vezes, em obra, o concreto é utilizado após este período. Com intuito de investigar o comportamento do concreto após o tempo de pega do cimento foram moldados seis traços de concreto com dois tipos de cimento. As misturas foram produzidas e mantidas no estado fresco por seis horas, adotando-se um procedimento de manutenção do abatimento através de aditivo superplastificante e agitação. Os resultados mostram que os corpos-de-prova moldados ao longo das seis horas mantiveram ou aumentaram a resistência à compressão média. |
| Databáze: |
OpenAIRE |
| Externí odkaz: |
|