Demirel, Münir; Diken Türksayar, Almira Ada; Donmez, Mustafa Borga (2023). Translucency, color stability, and biaxial flexural strength of advanced lithium disilicate ceramic after coffee thermocycling. Journal of esthetic and restorative dentistry, 35(2), pp. 390-396. Wiley 10.1111/jerd.12960 |
| DOI: |
10.48350/172694 |
| Popis: |
Objective To compare the color stability, translucency, and biaxial flexural strength (BFS) of differently glazed advanced lithium disilicate (ALDS) with those of lithium disilicate (LDS) and zirconia-reinforced lithium silicate (ZLS) after coffee thermocycling. Materials and methods Forty disk-shaped specimens were prepared from three lithium silicate based materials (CEREC Tessera, ALDS; IPS e.max CAD, LDS; Vita Suprinity, ZLS). ALDS specimens were divided into two subgroups according to glazing procedures (reduced glaze duration, ALDS-S and normal glaze duration, ALDS-N), while LDS and ZLS specimens were crystallized and glazed. Color coordinate measurements were performed before and after coffee thermocycling. Color differences (Delta E-00) and relative translucency parameters (RTP) were calculated. Specimens were then subjected to BFS test. Statistical analysis was performed by using 1- (Delta E-00 and BFS) and 2-way (RTP) ANOVA tests (alpha = 0.05). Results Delta E-00 values of tested materials were similar (df = 3, F = 0.150, p = 0.929). Two-way ANOVA showed the significant effect of material type, coffee thermocycling, and the interaction between these parameters on RTP values (p < 0.001). Both before and after thermocycling, LDS had the highest (p = 0.201). ZLS had the highest BFS (p |
| Databáze: |
OpenAIRE |
| Externí odkaz: |
|