Fracture strength of electroslag welding joint with high-performance steel
| Autor: | Satoshi Yamada, Hiroumi Shimokawa, Masato Nikaido, Yuka Matsumoto, Takumi Ishii, Jun Iyama |
|---|---|
| Rok vydání: | 2019 |
| Předmět: |
Toughness
Materials science business.industry Metals and Alloys Charpy impact test 020101 civil engineering 02 engineering and technology Building and Construction Welding Structural engineering Flange 0201 civil engineering law.invention 020303 mechanical engineering & transports 0203 mechanical engineering Mechanics of Materials law Electroslag welding Ultimate tensile strength business Ductility Joint (geology) Civil and Structural Engineering |
| Zdroj: | Journal of Constructional Steel Research. 153:495-508 |
| ISSN: | 0143-974X |
| DOI: | 10.1016/j.jcsr.2018.11.010 |
| Popis: | Τo clarify the fracture behavior of electroslag welding (ESW) joints, we used the connection of box-column flange and interior diaphragm made of high-performance steel SA440C. Owing to the large heat input, the ductility and notch toughness of ESW joints are prone to degradation. In particular, because the mechanical properties of high-strength steel are sensitive to the high heat input, the performance of ESW joints may significantly degrade when used with SA440C. In addition, considering the case wherein the beam-to-column connection is under strong seismic excitation, an ESW joint located at the crossing of a column flange, beam flange, and interior diaphragm is subject to biaxial tensile forces, causing premature brittle fracturing. To clarify the performance of ESW joints under such conditions, biaxial tensile loading tests were conducted. Four specimens were fabricated from the built-up box column, with interior diaphragms welded by ESW. Tensile load was statically applied between the interior diaphragm and the beam flange under constant axial load in the column flange. The maximum strength was demonstrated to be governed by the Charpy V-notch (CVN) toughness at the fractured locations. With regard to CVN toughness at the test temperature of the heat-affected zone or weld metal larger than 50 J, the maximum strength was comparable to that of the base metal of SA440C. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect