| Autor: | Antonio Forn, Mª Teresa Baile, S. Menargues |
|---|---|
| Přispěvatelé: | Universitat Politècnica de Catalunya. Departament de Ciència dels Materials i Enginyeria Metal·lúrgica, Universitat Politècnica de Catalunya. CDAL - Centre de Disseny d'Aliatges Lleugers i Tractaments de Superfície |
| Jazyk: | angličtina |
| Rok vydání: | 2013 |
| Předmět: |
lcsh:TN1-997
Materials science Silicon Alloy Metalls -- Tractament tèrmic chemistry.chemical_element Mineralogy semisólido engineering.material A356 Heat treatment A357 Alumini -- Aliatges -- Propietats mecàniques Aluminum alloys--Heat treatment Aluminium tratamientos térmicos Tratamientos térmicos Semisólido Materials Chemistry Semi-solid Physical and Theoretical Chemistry Dissolution lcsh:Mining engineering. Metallurgy Eutectic system Alkaline earth metal Aluminio a356 Mining engineering. Metallurgy a357 Magnesium Metallurgy Metals and Alloys TN1-997 aluminio Condensed Matter Physics Enginyeria dels materials::Materials compostos [Àrees temàtiques de la UPC] Enginyeria dels materials::Metal·lúrgia [Àrees temàtiques de la UPC] chemistry Metals--Semisolid processing engineering Heat treated Aluminum |
| Zdroj: | Revista de Metalurgia, Vol 49, Iss 4, Pp 266-274 (2013) Recercat. Dipósit de la Recerca de Catalunya Universitat Jaume I UPCommons. Portal del coneixement obert de la UPC Universitat Politècnica de Catalunya (UPC) |
| ISSN: | 1988-4222 0034-8570 |
| Popis: | In this work the microstructural changes that occurs during the solution and aging steps of heat treated of AlSi alloys, conformed in semi-solid state, were analysed. The study allowed developing a new T6 heat treatment, with solution times down to 30 min. With this new short heat treatment, the alloy showed better mechanical properties in comparison with the same alloy heat treated in standard conditions (solution times between 6 h and 8 h). This new heat treatment, carried out at 540 ºC, allowed complete magnesium dissolution and, at the same time, minimizes the grain and eutectic silicon growth. Although this experimentation was carried out with A356 and A357 aluminum alloys, conformed by Sub-Liquidus-Casting process, these results may be applicable to components produced with other semi-solid technologies and with others AlSi hardenable alloys that form coherent magnesium precipitates. The characterization of samples was carried out by micrographic analysis, by hardness and ultramicrohardnes tests.Se estudian los cambios microestructurales que tienen lugar en los tratamientos térmicos de las aleaciones AlSi, conformadas en estado semisólido, durante las etapas de puesta en solución y envejecimiento. El estudio ha permitido proponer nuevos tratamientos T6, con tiempos de puesta en solución inferiores a los 30 min, manteniendo o mejorando las propiedades mecánicas que se obtienen con los actuales procesos de tratamiento de 6 a 8 h. Estos tratamientos de corta duración, realizados a 540 ºC, permiten una completa disolución del magnesio, minimizando al mismo tiempo el crecimiento de los granos y del silicio eutéctico. Si bien la experimentación se ha realizado con componentes producidos por Sub-Liquidus Casting (SLC) con aleaciones A356 y A357, se considera que los resultados obtenidos pueden ser aplicables a los componentes producidos en estado semisólido por otras tecnologías, con diferentes aleaciones AlSi que se endurecen por formación de precipitados coherentes de magnesio. La caracterización del material se ha realizado mediante análisis micrográficos, ensayos de dureza y ultramicrodureza. |