Damage identification parameters of dual-phase 600–800 steels based on experimental void analysis and finite element simulations
| Autor: | Daniel Abbott Albertacci, Lílian Barros da Silveira, Fabiane Roberta Freitas da Silva, Marcelo Costa Cardoso, Andersan dos Santos Paula, Luciano Pessanha Moreira, Rafael Oliveira Santos |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2019 |
| Předmět: |
010302 applied physics
lcsh:TN1-997 Void (astronomy) Materials science Scanning electron microscope Metals and Alloys Nucleation Forming processes 02 engineering and technology Plasticity 021001 nanoscience & nanotechnology 01 natural sciences Finite element method Surfaces Coatings and Films Biomaterials visual_art 0103 physical sciences Ceramics and Composites visual_art.visual_art_medium Grain boundary Composite material 0210 nano-technology Sheet metal lcsh:Mining engineering. Metallurgy |
| Zdroj: | Journal of Materials Research and Technology, Vol 8, Iss 1, Pp 644-659 (2019) |
| ISSN: | 2238-7854 |
| Popis: | In this work, the damage behavior of cold-rolled zinc-coated dual-phase steel sheets 600 and 800 grades was evaluated by means of standard uniaxial tensile testing, microstructural characterization and finite element modeling. The void formation in both steels was investigated as a function of the plastic strain level from digital image processing of scanning electron micrographs to quantify the average void size and to determine the corresponding measures of void density, void area fraction and void aspect ratio. Based on the void analysis and the experimental uniaxial tensile test data, a four-step procedure is proposed to identify the parameters of the Gurson–Tvergaard–Needleman (GTN) damage model. Bearing in mind the non-uniqueness of the GTN model parameters, 3D finite element simulations using a single element and an 1/8 symmetry uniaxial tensile specimen model were performed in a systematic manner to investigate the role of both nucleation and failure parameters on the uniaxial behavior. At low straining levels, most of the void initiated by debonding of globular aluminum-oxide inclusions identified by EDS in both dual-phase steels. At higher straining levels, the void density evolution is found to be more pronounced in DP600 steel owing to the faster void nucleation rate at the ferrite grain boundaries. A good agreement between predictions and experimental load-elongation is achieved allowing for the identification of the full set of GTN damage model parameters of both DP600 and DP800 steels. The proposed damage calibration of dual-phase steels can be very helpful in simulations of practical sheet metal forming processes. Keywords: Dual-phase steels, Void analysis, Finite element modeling, Damage, Sheet metal forming |