0209 industrial biotechnology laser powder bed fusion Materials science maraging steel 02 engineering and technology engineering.material Article law.invention 020901 industrial engineering & automation law General Materials Science Selective laser melting Composite material Maraging steel Microscopy QC120-168.85 Fusion Bearing (mechanical) QH201-278.5 Isotropy dry sliding wear Tribology Engineering (General). Civil engineering (General) 021001 nanoscience & nanotechnology Laser TK1-9971 Descriptive and experimental mechanics selective laser melting Ball (bearing) engineering Electrical engineering. Electronics. Nuclear engineering TA1-2040 0210 nano-technology human activities additive manufacturing |
| Zdroj: | Materials Volume 14 Issue 10 Materials, Vol 14, Iss 2588, p 2588 (2021) |
| ISSN: | 1996-1944 |
| Popis: | This study aims to explore the wear performance of maraging 18Ni-300 steel, fabricated via laser powder bed fusion (LPBF). The building direction dependence of wear resistance was investigated with various wear loads and in terms of ball-on-disk wear tests. The effect of direct aging heat treatment, i.e., aging without solution heat treatment, on the wear performance was investigated by comparing the wear rates of directly aged samples, followed by solution heat treatment. The effect of counterpart material on the wear performance of the maraging steel was studied using two counterpart materials of bearing steel and ZrO2 balls. When the bearing steel ball was used as the counterpart material, both the as-built and heat-treated maraging steel produced by the LPBF showed pronounced building direction dependence on their wear performance when the applied wear load was sufficiently high. However, when the ZrO2 ball was used as the counterpart material, isotropic wear resistance was reported. The maraging steel produced by the LPBF demonstrated excellent wear resistance, particularly when it was aging heat-treated and the counterpart material was ZrO2. The directly aged sample showed wear performance almost the same as the sample solution heat-treated and then aged, indicating that direct aging can be used as an alternative post heat treatment for tribological applications of the maraging steels produced by LPBF. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|