Physicochemical properties and dentin bond strength of a tricalcium silicate-based retrograde material
| Autor: | Juliane Maria Guerreiro-Tanomaru, Raqueli Viapiana, Roberta Bosso-Martelo, Mário Tanomaru-Filho, Josette Camilleri, Camila de Paula Telles Pires Lucas |
|---|---|
| Přispěvatelé: | Universidade Estadual Paulista (Unesp), University of Malta |
| Jazyk: | angličtina |
| Rok vydání: | 2017 |
| Předmět: |
0301 basic medicine
Mineral trioxide aggregate Materials science Physicochemical properties Radiodensity Root canal Dentistry Root Canal Filling Materials 03 medical and health sciences chemistry.chemical_compound 0302 clinical medicine Materials Testing Dentin medicine Humans Composite material General Dentistry Cement business.industry Bond strength Silicates Tricalcium silicate 030206 dentistry Calcium Compounds 030104 developmental biology medicine.anatomical_structure Compressive strength chemistry Zinc oxide eugenol Dentin bond strength business |
| Zdroj: | Scopus Repositório Institucional da UNESP Universidade Estadual Paulista (UNESP) instacron:UNESP Brazilian Dental Journal v.28 n.1 2017 Brazilian Dental Journal Fundação Odontológica de Ribeirão Preto (FUNORP) instacron:FUNORP Brazilian Dental Journal, Volume: 28, Issue: 1, Pages: 51-56, Published: FEB 2017 |
| Popis: | The aim of this study was to evaluate the physicochemical properties and the apical dentin bond strength of the tricalcium silicate-based Biodentine in comparison to white MTA and zinc oxide eugenol-based cement (ZOE). Setting time and radiopacity were evaluated according to ISO 6876:2012 specification. Final setting time, compressive strength and pH were also assessed. Material’s bond strength to the apical root canal dentin was measured by the push-out assay. Data were analyzed by ANOVA and Tukey-Krammer post-hoc test. Biodentine presented the shortest initial (16.2±1.48 min) and final setting time (35.4±5.55 min). Radiopacity of Biodentine (2.79±0.27 mmAl) does not agree with ISO 6876:2012 specifications. On the other hand, Biodentine showed higher compressive strength after 21 days (37.22±5.27 MPa) and higher dentin bond strength (11.2±2.16 MPa) in comparison to white MTA (27.68±3.56 MPa for compressive strength and 2.98±0.64 MPa for bond strength) (p0.05) compared to ZOE (pH 7). It may be concluded that Biodentine exhibited faster setting, higher long-term compressive strength and bond strength to the apical dentin than MTA and ZOE. Resumo O objetivo deste estudo foi avaliar as propriedades físico-químicas e a resistência de união à dentina apical do cimento Biodentine em comparação ao MTA branco e cimento à base de óxido de zinco e eugenol (OZE). O tempo de presa e a radiopacidade foram avaliados de acordo com as especificações ISO 6876:2012. O tempo de presa final, a resistência à compressão e o pH também foram avaliados. A resistência de união dos materiais à dentina apical do canal radicular foi avaliada por meio do ensaio push-out. Dados foram analisados por ANOVA e teste complementar de Tukey-Krammer. Biodentine apresentou o menor tempo de presa inicial (16,2±1,48 min) e final (35,4±5,55 min). Os valores de radiopacidade do Biodentine (2,79±0,27 mmAl) não estão de acordo com as especificações ISO 6876:2012. Por outro lado, este material apresentou maior resistência à compressão após 21 dias (37,22±5,27 MPa) e maiores valores de adesão à dentina (11,2±2,16 MPa) em comparação ao MTA branco (27,68±3,56 MPa de resistência à compressão e 2,98±0,64 MPa de resistência de união) (p>0.05). Ambos os materiais produziram ambiente alcalino (aproximadamente 10) (p>0.05) em comparação ao OZE (pH 7). Pode-se concluir que o Biodentine demonstrou endurecimento mais rápido e apresentou maior resistência à compressão e resistência de união à dentina apical do que MTA e OZE. |