Corrosion characterization and ion release in SLM-manufactured and wrought Ti6Al4V alloy in an oral environment
| Autor: | Bajt Leban, Mirjam, Kosec, Tadeja, Finšgar, Matjaž |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2022 |
| Předmět: |
History
corrosion Polymers and Plastics Ti6Al4V SLM corrosion ion release XPS ToF-SIMS General Chemical Engineering Ti6Al4V General Chemistry ion release Industrial and Manufacturing Engineering SLM korozija udc:544.5/.6 XPS General Materials Science Business and International Management ToF-SIMS Ti6Al4V SLM korozija sproščanje ionov XPS ToF SIMS sproščanje ionov ToF SIMS |
| Zdroj: | Corrosion science, vol. 209, pp. 1-15, 2022. Corrosion science, str. 1-15, 2022, Vol. 209 COBISS-ID: 5881607 |
| ISSN: | 0010-938X |
| Popis: | As-produced and heat-treated TiAlV samples were prepared by selective laser melting and compared to wrought samples of identical chemical composition. Microstructural, corrosion, and spectroscopic studies of additively manufactured samples in artificial saliva at 37 °C, with NaF and at pH 2.3 were as a novelty combined with metal ion release during 42 days immersion. In artificial saliva higher amount of ions was released on SLM specimen when compared to wrought alloy. The total amount of ions released from SLM specimen in AS containing NaF was 10-times higher than in AS, while in AS with lactic acid it was 100-times higher. Št. članka 110716. Abstract. Bibliografija: str. 14-15. |
| Databáze: | OpenAIRE |