Transverse microhardness of artificial teeth
| Autor: | Regina Tamaki, Rafael Yague Ballester, Ricardo Jun Furuyama, Carolina Mayumi Iegami, Priscila Nakasone Uehara |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2015 |
| Předmět: |
Materials science
business.industry Acrylic Resins Dentistry Artificial Tooth Indentation hardness Mandibular second molar Wear resistance Transverse plane Dureza Hardness Tukey's range test Knoop hardness test Resinas Acrílicas General Earth and Planetary Sciences Composite material business Dente Artificial General Environmental Science |
| Zdroj: | Clinical and Laboratorial Research in Dentistry; Vol. 21 No. 4 (2015); 204-210 Clinical and Laboratorial Research in Dentistry; v. 21 n. 4 (2015); 204-210 Clinical and Laboratorial Research in Dentistry Universidade de São Paulo (USP) instacron:USP |
| ISSN: | 2357-8041 |
| Popis: | Objetivo: A dureza é tida como indicador de várias propriedades mecânicas de dentes artificiais, e relacionada a resistência ao desgaste. O objetivo foi mapear a microdureza de dentes artificiais de 9 marcas em função da profundidade. Método: foi medida a microdureza Knoop de segundos molares cortados num plano sagital em intervalos de 200 µm a partir da profundidade de 100 µm até 4700 µm, das marcas: Premium (Pr), Orthosit (Or), SR Postaris DCL (Po), Biotone (Bi), Artiplus IPN (Ar), VITA MFT (Vi), Natusdent (Na), Trilux (Tr) and Biolux (Bx). A ANOVA de medidas repetidas e o teste de Tukey (5%) analisaram os resultados. Resultados: A marca SR Orthosit PE apresentou a maior dureza (até a profundidade de 3,1 mm foi da ordem de 30 N/mm2), significativamente maior que todas as outras medidas realizadas (da ordem de 20 N/mm2). Conclusões: A dureza Knoop não evidenciou diferenças entre camadas para oito das nove marcas estudadas. Foi constatada diferente dureza entre a superfície e a região cervical para a marca SR Orthosit PE. Objective: Hardness is an indicator of several mechanical properties of artificial teeth, also related to wear resistance. The purpose of this article is to map the microhardness of artificial teeth as a function of depth and commercial brand. Methods: Knoop microhardness of sectioned artificial second molars was measured every 200 µm starting at a depth of 100 µm up until 4700 µm of the following brands: Premium (Pr), Orthosit (Or), SR Postaris DCL (Po), Biotone (Bi), Artiplus IPN (Ar), VITA MFT (Vi), Natusdent (Na), Trilux (Tr), and Biolux (Bx). Results were analyzed with ANOVA for repeated measures and Tukey test (5%). Results: SR Orthosit PE commercial brand presented higher hardness values (until the depth of 3.1 mm was 30 N/mm2), significantly higher than the other brands analyzed. Conclusion: Knoop hardness did not present differences between layers for eight of the nine brands studied. Different hardness values were found between superficial and cervical areas for the brand SR Orthosit PE. |