Local weld geometry-based characterization of fatigue strength in laser-MAG hybrid welded joints

Autor: Abinab Niraula, Heikki Remes, Pauli Lehto
Přispěvatelé: Marine and Arctic Technology, Department of Mechanical Engineering, Aalto-yliopisto, Aalto University
Rok vydání: 2023
Předmět:
Zdroj: Welding in the World. 67:1527-1544
ISSN: 1878-6669
0043-2288
Popis: openaire: EC/H2020/723246/EU//RAMSSES Funding Information: Open Access funding provided by Aalto University. This research was funded by Aalto University, Meyer Turku Oy, and the RAMSSES project (funded by the European Union’s Horizon 2020, grant agreement No. 723246), and the CaNeLis project (funded by the Business Finland, grant No. 3409/31/2022). The financial support is gratefully acknowledged. Publisher Copyright: © 2023, The Author(s). Thisresearch studies the influence of local weld notch parameters on fatigue crack initiation sites in laser-hybrid butt welds, utilizing high-resolution 3D scans and fatigue tests to failure. The suitability of different local geometric weld notch parameters for fatigue strength characterization is investigated, and the current challenges associated with their measurements are highlighted. The weld notch shapes were found to fluctuate significantly, resulting in considerable variation in notch parameters over short intervals. Undercut depth was found to determine the critical location for crack initiation. There were several instances where the fatigue crack initiated from notches with large radii despite the presence of sharper notches, contrary to what is expected on the basis of previous investigations. The results of the present study indicate that the undercut depth is a suitable fatigue strength indicator for high-quality laser-MAG hybrid welds, overcoming the practical limitations of notch radius measurement.
Databáze: OpenAIRE
Externí odkaz: