Influence of surface treatments on topography and bond strength of densely-sintered zirconium-oxide ceramic
Autor: | Laís Regiane da Silva Concílio, Ana Christina Claro Neves, Gabrielle Alencar Ferreira Silva, Elidineide Cruz da Luz, Leonardo Gonçalves Cunha, Frederico dos Reis Goyatá, Rafael Pino Vitti |
---|---|
Přispěvatelé: | Vitti, Rafael https://orcid.org/0000-0001-6366-5868, Silva Concilio, Lais https://orcid.org/0000-0002-3054-3810, Silva, Gabrielle Alencar Ferreira https://orcid.org/0000-0001-7663-581X, Vitti, Rafael/K-4931-2012 |
Rok vydání: | 2016 |
Předmět: |
Materials science
Alumina Materials Science Adhesive Cement Restorations 02 engineering and technology Surface finish Luting Cements Durability Failure Analysis 03 medical and health sciences chemistry.chemical_compound 0302 clinical medicine Materials Chemistry Cubic zirconia Ceramic Composite material Resin Bond strength Atomic force microscopy Process Chemistry and Technology Systems Fixed Partial Dentures 030206 dentistry Clinical Considerations 021001 nanoscience & nanotechnology Silane Surfaces Coatings and Films Electronic Optical and Magnetic Materials Surfaces chemistry Chemical Properties visual_art Ceramics and Composites visual_art.visual_art_medium Zirconium oxide Conditioning Methods Profilometer Strength 0210 nano-technology Materials Science Ceramics |
Zdroj: | Web of Science Repositório Institucional da UNITAU Universidade de Taubaté (UNITAU) instacron:UNITAU |
Popis: | Made available in DSpace on 2019-09-12T16:53:35Z (GMT). No. of bitstreams: 0 Previous issue date: 2016 The aim of this study was to evaluate the effect of surface treatments on the roughness and bond strength of dental materials containing MDP to zirconium oxide ceramic. Forty square-shaped zirconium-oxide ceramic blocks (Lava Zirconia, 3M-ESPE) were treated as follows: (CT) polished only; (SB) sandblasting (110 mu m aluminum oxide particles) or (SC) silica coating (110 gm particles). Roughness of treated surface was measured using a profilometer (Ra) and by atomic force microscope (AFM). Two resin luting agents were used after silane application: self-adhesive (Rely X U200, 3M-ESPE) and dual cure (Rely X Ultimate, 3M-ESPE). The samples were submitted to microshear bond strength test. The failure analysis was performed. Data were submitted to ANOVA and Tukey test (alpha=0.05). Bond strength results ranged from 20.44 (CT+Ultimate) to 34.37 MPa (SC+ U200) after 24 h and from 12.03 (CT+ Ultimate) to 27.44 MPa (SC+ U200) after 12 months of storage with SC statistically superior to the other treatments. Mean values of roughness varied from 0.07 (Cr) to 0.85 mu m (SC). The both resin luting agents showed similar results to all surface treatment groups. Silica coating provided the best treatment of the ceramic surface. (C) 2016 Elsevier Ltd and Techna Group S.r.l. All rights reserved. [Ferreira Silva, Gabrielle Alencar; da Luz, Elidineide Cruz; Cunha, Leonardo Goncalves] Univ Fed Bahia, Dept Restorat Dent, Salvador, BA, Brazil [Goyata, Frederico dos Reis] Univ Fed Minas Gerais, Dept Prosthodont, Belo Horizonte, MG, Brazil [da Silva Concilio, Lais Regiane; Claro Neves, Ana Christina; Vitti, Rafael Pino] Universidade de Taubaté (Unitau), Dept Prosthodont, BR-12020270 Taubate, SP, Brazil |
Databáze: | OpenAIRE |
Externí odkaz: |