Impact of the Porosity from Incremental and Bulk Resin Composite Filling Techniques on the Biomechanical Performance of Root-Treated Molars

Autor: P V Soares, Lrs Oliveira, A.A. Bicalho, Carlos José Soares, Luciana Mendes Barcelos, Ras Pereira
Rok vydání: 2021
Předmět:
Zdroj: Operative Dentistry. 46:197-207
ISSN: 1559-2863
0361-7734
DOI: 10.2341/19-297-l
Popis: SUMMARY Objectives: To analyze the effect of the porosity caused by incremental and bulk resin composite filling techniques using low- and high-viscosity composite resins on the biomechanical performance of root-treated molars. Methods: Forty intact molars received standardized mesio-occlusal-distal (MOD) cavity preparation, were root treated, and randomly divided into four groups with different filling techniques (n=10). The first involved two incremental filling techniques using VIT/Z350XT, a nanofilled composite resin (Filtek Z350XT, 3M ESPE) associated with a resin-modified glass ionomer cement, and resin-modified glass ionomer cement (RMGIC; Vitremer, 3M ESPE) for filling the pulp chamber. The second involved TPH/VIT, a microhybrid composite resin TPH3 Spectrum associated with Vitremer. The third and fourth involved two bulk-fill composite resins: SDR/TPH, a low-viscosity resin composite (Surefill SDR flow, Dentsply) associated with TPH3 Spectrum, and POST, a high-viscosity bulk-fill resin composite (Filtek Bulk Fill Posterior, 3M ESPE). The volume of the porosity inside the restoration was calculated by micro-CT. The cusp deformation caused by polymerization shrinkage was calculated using the strain-gauge and micro-CT methods. The cusp deformation was also calculated during 100 N occlusal loading and loading to fracture. The fracture resistance and fracture mode were recorded. Data were analyzed by one-way analysis of variance and Tukey test. The fracture mode was analyzed by the χ2 test. The volume of the porosity was correlated with the cusp deformation, fracture resistance, and fracture mode (a=0.05). Results: Incremental filling techniques associated with RMGIC resulted in a significantly higher porosity than that of both bulk-fill techniques. However, no significant difference was found among the groups for the fracture resistance, fracture mode, and cusp deformation, regardless of the measurement time and method used. No correlation was observed between the volume of the porosity and all tested parameters. Conclusions: The porosity of the restorations had no influence on the cuspal deformation, fracture resistance, or fracture mode. The use of the RMGIC for filling the pulp chamber associated with incremental composite resins resulted in similar biomechanical performance to that of the flowable or regular paste bulk-fill composite resin restorations of root-treated molars.
Databáze: OpenAIRE
Externí odkaz: