Evaluation of shear bond strength between dual cure resin cement and zirconia ceramic after thermocycling treatment
| Autor: | Jung-Jin Lee, Ju-Won Oh, Cheol-Kyun Kang, Ju-Mi Park, Jae-Min Seo |
|---|---|
| Rok vydání: | 2015 |
| Předmět: | |
| Zdroj: | The Journal of Advanced Prosthodontics |
| ISSN: | 2005-7814 2005-7806 |
| DOI: | 10.4047/jap.2015.7.1.1 |
| Popis: | PURPOSE. This study was performed to evaluate shear bond strength (SBS) between three dual-cured resin cements and silica coated zirconia, before and after thermocycling treatment. MATERIALS AND METHODS. Sixty specimens were cut in 15 x 2.75 mm discs using zirconia. After air blasting of 50 μm alumina, samples were prepared by tribochemical silica coating with RocatecTM plus. The specimens were divided into three groups according to the dual-cure resin cement used: (1) Calibra silane+Calibra® , (2) Monobond S+Multilink ® N and (3) ESPN sil+RelyXTM Unicem Clicker. After the resin cement was bonded to the zirconia using a Teflon mold, photopolymerization was carried out. Only 10 specimens in each group were thermocycled 6,000 times. Depending on thermocycling treatment, each group was divided into two subgroups (n=10) and SBS was measured by applying force at the speed of 1 mm/min using a universal testing machine. To find out the differences in SBS according to the types of cements and thermocycling using the SPSS, two-way ANOVA was conducted and post-hoc analysis was performed by Turkey’s test. RESULTS. In non-thermal aged groups, SBS of Multilink group (M1) was higher than that of Calibra (C1) and Unicem (U1) group (P |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|