Wear Resistance of Fe-based Nanostructured Hardfacing
| Autor: | Estela Surian, Cristian Marini, Hernán Gabriel Svoboda, Agustín Gualco |
|---|---|
| Rok vydání: | 2015 |
| Předmět: | |
| Zdroj: | CIC Digital (CICBA) Comisión de Investigaciones Científicas de la Provincia de Buenos Aires instacron:CICBA |
| ISSN: | 2211-8128 |
| DOI: | 10.1016/j.mspro.2015.04.154 |
| Popis: | The purpose of this work was to study the microstructural evolution and wear resistance of a nanostructured iron-based alloy deposited by FCAW process. Two samples with one and two layers were welded under Ar-20CO2 shielding and heat input of 3.5 kJ/mm. Chemical composition was determined and microstructure was studied using both optical and scanning electron microscopy and X ray diffraction. Hardness, cristallite size, percentage of dilution and abrasive wear resistance were measured. The hardness of the deposit was found between 800 and 920 HV2, depending on the number of layers as well as the chemical composition of the samples. The wear test results were discussed in relation to chemical composition, microstructure and hardness. Fil: Gualco, Agustín. Universidad Nacional de Lomas de Zamora. Facultad de Ingeniería. Secretaria de Investigación; Argentina Fil: Marini, Cristian. Universidad Nacional de Lomas de Zamora. Facultad de Ingeniería. Secretaria de Investigación; Argentina Fil: Svoboda, Hernán Gabriel. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería "Hilario Fernández Long". Universidad de Buenos Aires. Facultad de Ingeniería. Instituto de Tecnologías y Ciencias de la Ingeniería "Hilario Fernández Long"; Argentina Fil: Surian, Estela Silvia. Universidad Nacional de Lomas de Zamora. Facultad de Ingeniería. Secretaria de Investigación; Argentina. Universidad Tecnológica Nacional. Facultad Regional San Nicolás. Centro para el Desarrollo Tecnológico de Materiales; Argentina |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|