Evaluación de las propiedades tribológicas de materiales compuestos de matriz metálica (MMCs) procesados por técnicas de fabricación aditiva con haz láser (SLM)
| Autor: | Octavio Andrés González-Estrada, Elkin Martínez, Alejandro Martínez |
|---|---|
| Přispěvatelé: | Universidad de Santander (UDES), Grupo de Investigación en Energía y Medioambiente [Bucaramanga]] (GIEMA), Universidad Industrial de Santander [Bucaramanga] (UIS), Instituto Tecnológico Metalmecánico, Mueble, Madera, Embalaje y Afines (AIDIMME) |
| Jazyk: | Spanish; Castilian |
| Rok vydání: | 2017 |
| Předmět: |
Engineering drawing
Materials science Scanning electron microscope Pharmaceutical Science Selective Laser Melting (SLM) lcsh:Technology Superficie de desgaste modelo Wear rate Fabricación aditiva (AM) Pharmacology (medical) Ceramic Selective laser melting Composite material Reinforcement Friction coefficient lcsh:T Metal matrix composites (MMCs) Fusión selectiva con láser (SLM) Tribology Tasa de desgaste Worn surface Ensayo “pin-on-disk” Pin-on-disk test Additive Manufacturing (AM) [SPI.MECA.STRU]Engineering Sciences [physics]/Mechanics [physics.med-ph]/Mechanics of the structures [physics.class-ph] Complementary and alternative medicine lcsh:TA1-2040 Coeficiente de fricción visual_art visual_art.visual_art_medium lcsh:Engineering (General). Civil engineering (General) Materiales compuestos de matriz metálica (MMCs) |
| Zdroj: | Revista UIS Ingenierías Revista UIS Ingenierías, Facultad de Ingenierías Fisicomecánicas de la Universidad Industrial de Santander, 2017, 16 (1), pp.101-114 Revista UIS Ingenierías, Vol 16, Iss 1 (2016) |
| ISSN: | 1657-4583 2145-8456 |
| Popis: | International audience; The mechanical and tribological properties of steel matrix composites (316L stainless steel reinforced with Cr3C2 ceramic particles) were investigated. The steel matrix composites (SMC) with three reinforcing percentages (3, 6, and 9 wt.%) were manufactured by Additive Manufacturing technologies (SLM: Selective Laser Melting). The wear behaviour was studied by using a pin-on-disk wear test at room temperature. The worn surface was analysed using Scanning Electron Microscopy (SEM). The results indicated that the friction coefficient does not have a clear tendency or direct correlation with the reinforcement variation while the wear rate decreases with increasing content of reinforcement. The better properties combination were achieved with 6 wt.% of reinforcement.; En este artículo se investigaron las propiedades mecánicas y tribológicas de materiales compuestos de matriz de acero (acero inoxidable 316L reforzado con partículas cerámicas Cr3C2) procesados por tecnologías de fabricación aditiva de fusión selectiva con láser (SLM). Se estudió el comportamiento a desgaste con el ensayo " pin-on-disk " a temperatura ambiente y se observó la superficie desgastada mediante microscopía electrónica de barrido (SEM). Los resultados indicaron que el coeficiente de fricción no tiene una tendencia clara o relación directa cuando se varía el porcentaje de refuerzo mientras que la tasa de desgaste disminuye con el aumento del contenido de refuerzo. Las mejores propiedades se obtuvieron con un 6% en peso de refuerzo. PALABRAS CLAVE: . |