Bulk Fill Kompozitlerin Mikrosertliklerinin Karşılaştırılması
| Autor: | Reyhan ŞİŞMAN, Burak DAYI, Hacer TURGUT, Enis ŞİMŞEK |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2022 |
| Předmět: | |
| Zdroj: | Volume: 10, Issue: 2 414-421 İnönü Üniversitesi Sağlık Hizmetleri Meslek Yüksek Okulu Dergisi |
| ISSN: | 2147-7892 |
| Popis: | The aim of this study is to compare the microhardness of five different bulk fill composites (SDR, TEC, XTF, SF, FBF). A total of 25 cylindrical molds were prepared. Composite resin was placed in each mold in sequence, at one time, by condensing it thoroughly. Then, the polymerization of the composites was achieved with the LED light device which was applied for 20 seconds. Microhardness measurements of the samples were made with the classical Vicker's test. The data of our study were evaluated by using the Kruskal Wallis H test with the SPSS 20.0 package program. When the measured surface microhardness values were compared between the groups; microhardness values SDR and FBF groups were found to be significantly lower than TEC, XTF and KSF groups (p Bu çalışmanın amacı beş farklı bulk fill kompozitin mikrosertliklerinin karşılaştırılmasıdır (SDR, TEC, XTF, SF, FBF). Toplam 25 adet silindirik kalıp hazırlandı. Sırası ile her bir kalıba tek seferde kompozit rezin iyice kondanse edilerek yerleştirildi. Daha sonra 20 sn uygulanan LED ışık cihazı ile kompozitlerin polimerizasyonu sağlandı. Örneklerin mikrosertlik ölçümleri klasik Vicker’s testi ile yapıldı. Çalışmamızın verileri SPSS 20.0 paket programı ile Kruskal Wallis H testi kullanılarak değerlendirildi. Ölçülen üst yüzey mikrosertlik değerleri gruplar arasında karşılaştırıldığında; SDR ve FBF grubunun mikrosertlik değeri, TEC, XTF ve KSF gruplarına göre anlamlı derecede daha düşük bulundu (p |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|