Effect of doping and crystallite size on the electrochemical performance of Li4Ti5O12
| Autor: | Jorma Jokiniemi, Anna Lähde, Tiina Torvela, Tommi Karhunen, Juho Välikangas, Ulla Lassi |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2016 |
| Předmět: |
Materials science
synthesis ta221 Nanoparticle chemistry.chemical_element Nanotechnology 02 engineering and technology engineering.material 010402 general chemistry 01 natural sciences Crystallinity chemistry.chemical_compound Materials Chemistry Li-ion battery Lithium titanate ta216 ta116 Quenching Mechanical Engineering Doping Spinel Metals and Alloys 021001 nanoscience & nanotechnology 0104 chemical sciences phase composition chemistry Chemical engineering Mechanics of Materials engineering Lithium nanoparticles Crystallite 0210 nano-technology |
| Zdroj: | Journal of Alloys and Compounds. 659:132-137 |
| ISSN: | 0925-8388 |
| Popis: | Defect spinel phase lithium titanate (Li 4 Ti 5 O 12 ) has been suggested as a promising negative electrode material for next generation lithium ion batteries. Flame spray pyrolysis has been shown to be a viable fast, one-step process for synthesis of nanoparticulate Li 4 Ti 5 O 12 . However, due to the rapid quenching that is integral to the process the crystallite size remain very small and non-uniform. To overcome this shortcoming a vertical flow tube furnace was used to increase the high-temperature residence time. This resulted in an increase in the crystallite size and crystallinity of the product. As a result of this increase the electrochemical performance of the Li 4 Ti 5 O 12 was markedly improved. Furthermore, silver doping of the Li 4 Ti 5 O 12 material can be carried out simultaneously with its synthesis in the FSP process. The resulting nanosized silver particles on the surface of the Li 4 Ti 5 O 12 particles further improve the electrochemical performance during high current operations. The specific capacities of these high-temperature synthesised pure and silver-doped Li 4 Ti 5 O 12 nanoparticles were found to increase by up to 6% and 19%, respectively, compared to a commercial reference. Thus the technique provides a simple method for synthesising superior quality Li 4 Ti 5 O 12 for battery applications. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect