Iron-based reversible adhesives: Effect of particles size on mechanical properties
| Autor: | Raffaele Ciardiello, Valentina Giovanna Brunella, Vg Lambertini, Brunetto Martorana |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2018 |
| Předmět: |
Materials science
Field (physics) Component (thermodynamics) Mechanical Engineering Adhesive hot-melt disbonding recyclability iron particles iron oxide particles single lap joint Adhesive 030206 dentistry 02 engineering and technology 021001 nanoscience & nanotechnology 03 medical and health sciences Hot-melt adhesive 0302 clinical medicine recyclability iron particles iron oxide particles Iron based disbonding hot-melt Composite material 0210 nano-technology Hot melt single lap joint |
| Popis: | A hot melt adhesive – mainly used for bonding plastic component in automotive field – was modified with different iron-based particles to give it a reversible behaviour. Mechanical and physical properties of these reversible adhesives were experimentally assessed in the work. The modified adhesives, coupled with electromagnetic induction, are able to guarantee separation of the joints without any damage to the substrates for recycling, reuse or repairing of components. Single lap joint specimens were prepared using epoxy/glass fibres substrates and tests were carried out on neat and modified adhesive with 5% weight of iron and iron oxide. Three different Fe particles size were tested: 450 µm, 60 µm and 1–6 µm. The particles size of iron oxide was 50 nm. Separation was studied using single lap joint specimens under electro-magnetic induction. Experimental results showed that the maximum peak load decreases when the average particles sizes increase. The peak loads of the smallest particles were equal to the ones of the pristine adhesive. The elongation of the adhesives increases when the adhesive is modified with both iron and iron oxide particles. Finally, experimental tests on single lap joints coupled with electro-magnetic induction showed that separation of the substrates is possible using iron oxide particles. Electro-magnetic tests conducted on particles alone, helped to understand that bigger particles are able to overcome the melting temperature of the adhesive but hot-melt adhesives modified with these particles are not able to reach the melting. These tests showed that the number of particles into the adhesive matrix is very important for this kind of tests. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|