Improvements in mechanical strength and thermal stability of injection and compression molded components based on Poly Lactic Acids
| Autor: | Annamaria Gisario, Clizia Aversa, M. Puopolo, Elisa Pizzi, Massimiliano Barletta, S. Vesco |
|---|---|
| Přispěvatelé: | Aversa, Clizia, Barletta, Massimiliano, Gisario, Annamaria, Pizzi, Elisa, Puopolo, Michela, Vesco, Silvia |
| Jazyk: | angličtina |
| Rok vydání: | 2018 |
| Předmět: |
Materials science
Polymers and Plastics General Chemical Engineering Plastics extrusion Compression molding melt processing 02 engineering and technology Molding (process) 010402 general chemistry 01 natural sciences compostable polymer mechanical response molding thermal stability law.invention Differential scanning calorimetry Flexural strength law Thermal stability Chemical Engineering (all) Crystallization Composite material chemistry.chemical_classification Organic Chemistry Polymer 021001 nanoscience & nanotechnology 0104 chemical sciences chemistry Settore ING-IND/16 - Tecnologie e Sistemi di Lavorazione 0210 nano-technology |
| Popis: | Degradable polymers are limited by their often-insufficient mechanical and thermal properties, which limit their usage to single-use packaging items at room temperature and in dry conditions. In this respect, the present work deals with the manufacture of custom-built Poly Lactic Acids (PLAs), which are designed to be compostable, suitable for food contact and are characterized by a good compromise between mechanical properties and thermal stability. A commercial grade PLA was, therefore, compounded in a twin-screw co-rotating extruder by the use of specific additives: maleated and glycidyl methacrylate PLAs as compatibilizers/chain extenders and microlamellar talc as mineral filler/nucleation promoter. After pelletizing, the resulting compounds were melt-processed by injection and compression molding. Differential scanning calorimetry, flexural tests in static machine and top-hat cylindrical flat indentations were performed to evaluate the thermal and mechanical response of the molded components. The experimental findings show that crystallization of the PLA can be controlled by fine-tuning the compound formulation as well as by properly setting the processing parameters. In addition, achievement of the appropriate crystallization degree in the polymer can lead to molded components, which exhibit improved mechanical strength and high thermal stability. |