Comparison of two methods for measuring the polymerization characteristics of flowable resin composites
| Autor: | Masashi Miyazaki, Hiroyasu Kurokawa, Toshiki Takamizawa, Akitomo Rikuta, Akira Yamamoto |
|---|---|
| Rok vydání: | 2007 |
| Předmět: |
Dental Stress Analysis
Analysis of Variance Materials science Light Viscosity Composite number Composite Resins Phase Transition Speckle pattern Polymerization Hardness Mechanics of Materials Materials Testing Scattering Radiation Bisphenol A-Glycidyl Methacrylate General Materials Science Irradiation Dilatometer Composite material Dental Restoration Permanent Rheology General Dentistry Curing (chemistry) Glass tube Power density |
| Zdroj: | Dental Materials. 23:792-798 |
| ISSN: | 0109-5641 |
| Popis: | Objectives The purpose of this study was to compare two methods for assessing the polymerization characteristics of flowable resin composites. Methods Two different flowable resin composites and a hybrid resin composite control were investigated. In order to measure the volumetric shrinkage (Δ V ), each material was placed into a mould and extruded into a water-filled dilatometer. The specimens were then light irradiated for 30 s using a curing unit with the power density adjusted to either 100 or 600 mW/cm 2 . For the speckle contrast measurement, each resin composite was condensed into a glass tube and irradiated. The laser–speckle field was recorded in a digital frame. The calculated values were obtained for each pair of adjacent patterns and the changes in speckle contrast as a function of time were obtained. Results The average Δ V values of the resins after 180 s ranged from ∼3.3 to 4.4% for the flowable composites and from ∼1.8 to 2.3% for the hybrid composite control. The overall magnitude of the speckle contrasts decreased soon after the initial light exposure commenced and gradually increased thereafter. The speckle contrast measurements revealed changes in the pastes due to the polymerization of the flowable resins that were greater than those obtained with the water-filled dilatometer. Significance These data suggest that the polymerization characteristics of flowable resins can be measured successfully using two different methods. Moreover, our findings are of clinical relevance, as the data obtained under laboratory conditions might give an indication of the suitability of flowable resin composites for specific clinical applications. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect