Microstructure, texture and hardness of Al–Cu–Li alloy sheet during hot gas forming with integrated heat treatment
| Autor: | Fan Xiaobo, P. Lin, Shijian Yuan, Zhubin He |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2016 |
| Předmět: |
0209 industrial biotechnology
Materials science Mechanical Engineering Metallurgy 02 engineering and technology 021001 nanoscience & nanotechnology Microstructure 020901 industrial engineering & automation Precipitation hardening Mechanics of Materials Vickers hardness test Dynamic recrystallization lcsh:TA401-492 Formability General Materials Science Grain boundary lcsh:Materials of engineering and construction. Mechanics of materials 0210 nano-technology Strengthening mechanisms of materials Electron backscatter diffraction |
| Zdroj: | Materials & Design, Vol 94, Iss, Pp 449-456 (2016) |
| ISSN: | 0264-1275 |
| Popis: | In this paper, hot gas forming with integrated heat treatment was carried out to investigate the microstructure and strengthening behavior of an Al–Cu–Li alloy sheet. The cup-shaped specimen was free bulged by compressed air within 3 s after the sheet was heated at 520 °C for 30 min. The corresponding strengthening behavior was reflected by Vickers hardness measurement. Microstructure observation was conducted to reveal the deformation and strengthening mechanisms by using electron backscatter diffraction and transmission electron microscope techniques. It was found that the hardness in the undeformed area could arrive at 181 HV, which increased as deformation increased. Dynamic recovery occurred while the effective strain was 0.31. Dynamic recrystallization occurred with further increase in deformation, accompanying with grain fragmentation. The grains in {110} orientation were produced gradually with increasing deformation. Precipitation strengthening was the main strengthening mechanism in the undeformed area, which could be enhanced by the deformation during hot gas forming. A high density of dislocations and low angle grain boundaries were produced in the deformed area, which accelerated more fine precipitates precipitating. Enhanced formability and hardness were obtained during rapid hot gas forming by combining with heat treatment. Keywords: Al–Cu–Li alloy, Quick plastic forming, Hot gas forming, Heat treatment, Microstructure |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect