Effect of fiber nets, application techniques and flowable composites on microleakage and the effect of fiber nets on polymerization shrinkage in class II MOD cavities
| Autor: | Emre Ozel, Mübin Soyman |
|---|---|
| Přispěvatelé: | Ozel, E., Soyman, M., Yeditepe Üniversitesi |
| Jazyk: | angličtina |
| Rok vydání: | 2009 |
| Předmět: |
Time Factors
Materials science Polymers Surface Properties medicine.medical_treatment Composite number Organophosphonates Coloring agents Materials testing Composite Resins Dental Materials Acid Etching Dental Materials Testing Rosaniline Dyes medicine Humans Fiber Composite material Coloring Agents Dental Restoration Permanent General Dentistry Shrinkage Dental Leakage Acid etching Dental Cavity Lining Temperature Resin Cements Polymerization Dentin-Bonding Agents Polyethylenes Dental Cavity Preparation Dental restoration |
| Popis: | This study evaluated the effects of fiber nets and application techniques and flowable composites as a liner on microleakage and the effects of fiber nets on polymerization shrinkage in Class II MOD cavities. Standard MOD cavities were performed in 80 extracted third molars. The teeth were randomly divided into eight groups (n=10). Group 1: Filtek Supreme XT (bulk technique) (FSB); Group 2: Filtek Supreme XT (incremental technique) (FSI); Group 3: Filtek Supreme XT Flow (FS Flow)+FSB; Group 4: FS Flow+FSI; Group 5: FS Flow+Ribbond (R)+FSB; Group 6: FS Flow+R+FSI; Group 7: FS Flow+everStick NET (E)+FSB; Group 8: FS Flow+(E)+FSI. All the teeth were then immersed in 0.5% basic fuchsin solution for 24 hours after thermocycling for 1000 cycles (5°C and 55°C). The teeth were sectioned longitudinally and observed under a stereomicroscope. In order to determine the polymerization shrinkage, another study was designed. In Group A, composite was applied as a bulk. In Group B, the resin composite was divided into two parts and Ribbond fiber was placed in the middle of the mass. In Group C, everStick NET fiber was placed inside the composite, as in Group B. Statistical analysis were performed by using one-way ANOVA and Tukey HSD tests for both microleakage and polymerization shrinkage (p |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|