Niobium oxide nanocolumns formed via anodic alumina with modulated pore diameters
| Autor: | A. Pligovka, A. Zakhlebayeva, Andrei Lazavenka |
|---|---|
| Rok vydání: | 2018 |
| Předmět: | |
| Zdroj: | Journal of Physics: Conference Series. 987:012006 |
| ISSN: | 1742-6596 1742-6588 |
| Popis: | Niobium oxide nanocolumns with modulated diameters were formed for the first time. An Al/Nb bilayer specimen was prepared by successive sputter-deposition of 300 nm niobium layer and 1200 nm aluminum layer onto silicon wafer. Regular anodic alumina matrix with modulated pore diameters was formed by sequential anodization of initial specimen in tartaric acid at 180 V, and in oxalic acid at 37 V. Further potentiodynamic reanodization of the specimen up to 400 V causes the simultaneous growth of 440 nm continuous niobium oxide layer beneath the alumina film and two types of an array of oxide nanocolumns (thick – with 100 nm width and 630 nm high and thin – with 25 nm width and 170 nm high), which are the filling of the alumina pores. The morphology of the formed anodic niobium oxide nanocolumns with modulated diameters was determined by field emission scanning electron microscopy. The formed nanostructures can be used for perspective devices of nano- and optoelectronics such as photonic crystals. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|