| Popis: |
Reinforcement corrosion rate and crack width relationship in concrete beams exposed to simulated marine environment ABSTRACT This investigation presents an empirical correlation between the rebar corrosion rate and the corrosion-induced crack width propagation rate produced on beam's concrete cover, with or without load application to these beams. Reinforced concrete beams were evaluated, exposed to a natural corrosion process by spraying with 3.5 %w/w NaCl solution, to accelerate the rebar corrosion process, was performed with electrochemical tests. The beams corrosion-cracking evaluation was performed once every month, to determine the relation between crack width and the rebar corrosion loss. The results showed a direct relation between crack width propagation and rebar corrosion rate, showing wider cracks in the loaded beams. Keywords: corrosion; reinforced concrete; loaded beams; crack widths. Relacion entre la velocidad de corrosion de la armadura y el ancho de fisuras en vigas de concreto armado expuestas a ambientes que simulan el medio marino RESUMEN Esta investigacion presenta una relacion empirica entre la velocidad de corrosion de la armadura y la velocidad de ensanchamiento de fisuras por corrosion del recubrimiento de concreto en vigas, con o sin aplicacion de carga. Se evaluaron vigas de concreto armado, expuestas a un proceso de corrosion natural mediante el rociado con solucion salina al 3,5 %p/p de NaCl, para acelerar el proceso corrosivo de la armadura, mediante ensayos electroquimicos. El ancho de fisuras se evaluo mensualmente para estimar la relacion existente entre este y la perdida de seccion de la armadura. Los resultados demuestran que existe una relacion directa entre la propagacion del ancho de fisuras y la velocidad de corrosion, observando fisuras de mayor ancho en vigas cargadas. Palabras clave: corrosion; concreto armado; vigas cargadas; ancho de fisuras. Relacao entre a velocidade de corrosao da armadura e a largura das fissuras em vigas de concreto armado expostas a ambientes que simulam o ambiente marinho RESUMO Esta pesquisa apresenta uma relacao empirica entre a taxa de corrosao da armadura e a abertura de fissuras por efeito da corrosao da armadura em vigas de concreto, com ou sem aplicacao de carga. Foram avaliadas vigas de concreto armado, expostas a um processo de corrosao natural por pulverizacao com solucao salina a concentracao de 3,5% de NaCl, para acelerar o processo de corrosao da armadura, mediante ensaios eletroquimicos. A abertura das fissuras foi avaliada mensalmente para estimar a relacao entre ela e a perda de secao da armadura. Os resultados mostram que existe uma relacao direta entre a propagacao da abertura da fissura e a taxa de corrosao, observando a ocorrencia de fissuras de maior abertura nas vigas sob carga. Palavras-chave: corrosao; vigas de concreto armado sob carga; abertura de fissuras. |