A new endodontic mixture based on calcium aluminate cement obtained by hydrothermal synthesis
| Autor: | Božana Čolović, Željko Žižak, Ognjenka Janković, Vukoman Jokanović, Slavoljub Živković, Irina Besu Žižak |
|---|---|
| Rok vydání: | 2019 |
| Předmět: |
Materials science
Scanning electron microscope Aluminate 02 engineering and technology 01 natural sciences Calcium aluminate chemistry.chemical_compound 0103 physical sciences Microscopy Materials Chemistry Hydrothermal synthesis 010302 applied physics Cement Alkaline earth metal Process Chemistry and Technology Biomedical application Chemical preparation 021001 nanoscience & nanotechnology Surfaces Coatings and Films Electronic Optical and Magnetic Materials Compressive strength chemistry X-ray crystallography Ceramics and Composites Strength Powders 0210 nano-technology Nuclear chemistry |
| Zdroj: | Ceramics International |
| ISSN: | 0272-8842 |
| Popis: | The synthesis of a new endodontic mixture based on calcium aluminate cement is reported. Physico-chemical and mechanical properties of the mixture were investigated before and after various hydration periods. Phase analysis of the mixture was performed using X-ray diffraction (XRD), while morphological analysis was performed by scanning electron microscopy (SEM) equipped with EDS which revealed elemental composition of the mixture sample. Investigations of mechanical properties showed that this new endodontic mixture possessed good mechanical properties (compressive strength after 28 days aging was 94 MPa) and relatively short setting time (2 h). Additionally, cytotoxicity of the mixture was investigated by MTT assay, while genotoxicity was investigated by Comet assay, using MRC-5 cell line. The obtained results make this material very promising for potential application in dental practice. © 2019 Elsevier Ltd and Techna Group S.r.l. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect