Photodegradation test of asphalt binder using pressed thin film samples
| Autor: | Iwao Sasaki, Katsuyuki Yamaguchi, Seishi Meiarashi |
|---|---|
| Rok vydání: | 2005 |
| Předmět: |
Materials science
asphalt binder thin film mince couche aging vieillissement liant routier rhéomètre de cisaillement dynamique (« dynamic shear rheometer : DSR ») FTIR Asphalt photodegradation Thin film Composite material photodégradation Photodegradation DSR General Environmental Science Civil and Structural Engineering |
| Zdroj: | Canadian Journal of Civil Engineering. 32:1166-1169 |
| ISSN: | 1208-6029 0315-1468 |
| DOI: | 10.1139/l05-068 |
| Popis: | The photodegradation behavior of a straight asphalt was investigated using a new method "photodegradation test of asphalt binder using pressed thin film samples". Although the photodegradation caused by outdoor exposure is limited to the near surface, the results confirmed that the degree of degradation during 1 to 2 months is more severe than that by the pressure aging vessel (PAV) test, which is designed to simulate the degradation that will occur in the asphalt pavement over 5 to 10 service years. Le comportement à la photodégradation d'un asphalte sans additif a été étudié en utilisant une nouvelle méthode, « essai de photodégradation d'échantillons de minces couches pressées de liant routier ». Bien que la photodégradation engendrée par l'exposition aux éléments soit peu profonde, les résultats ont confirmé que le niveau de dégradation durant 1 à 2 mois est plus élevé que celui indiqué par l’essai de vieillissement PAV (pressure aging vessel) qui est conçu pour simuler la dégradation du revêtement en asphalte durant une période de 5 à 10 ans. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|