Síntesis de sílice mesoestructurada: determinación de las condiciones óptimas de extracción del templato
| Autor: | Monica Liliana Parentis, Elio Emilio Gonzo, Melisa Romina Serrano, Delicia Ester Acosta, Agustina María Pía Gramaglia Saracho, Norberto Alejandro Bonini |
|---|---|
| Jazyk: | Spanish; Castilian |
| Rok vydání: | 2018 |
| Předmět: |
Sílice mesoporosa
Chemistry TEOS General Physics and Astronomy 02 engineering and technology General Chemistry CTAB INGENIERÍAS Y TECNOLOGÍAS 010402 general chemistry 021001 nanoscience & nanotechnology MCM-41 01 natural sciences 0104 chemical sciences técnica sol-gel Ingeniería Química purl.org/becyt/ford/2.4 [https] MESOPOROUS SILICA purl.org/becyt/ford/2 [https] Otras Ingeniería Química General Materials Science SOL-GEL TECHNIQUE 0210 nano-technology Humanities |
| Zdroj: | Matéria (Rio de Janeiro), Volume: 23, Issue: 2, Article number: 12131, Published: 19 JUL 2018 Matéria (Rio de Janeiro) v.23 n.2 2018 Matéria (Rio de Janeiro. Online) instacron:RLAM CONICET Digital (CONICET) Consejo Nacional de Investigaciones Científicas y Técnicas instacron:CONICET |
| Popis: | Se sintetizó sílice mesoporosa a través del proceso sol-gel usando tetraetoxisilano (TEOS) como fuente de sílice y bromuro de n-hexadeciltrimetilamonio (CTAB) como agente director de la estructura. La eliminación del surfactante post-síntesis, se realizó mediante dos técnicas: calcinación con incrementos programados de temperatura hasta alcanzar los 550°C y extracción con solventes usando HCl/EtOH como solución extractora y modificando algunas variables experimentales, tales como la concentración del ácido, el volumen de solución extractora, la duración del tratamiento y el solvente empleado para realizar el lavado. Las muestras fueron caracterizadas por adsorción de nitrógeno, espectroscopia de IR y SEM. Tanto la técnica de síntesis empleada como los procedimientos para eliminar el surfactante conducen a un material del tipo MCM-41. Mediante calcinación se obtienen materiales con un área superficial de 1100 m2 /g mientras que la extracción con HCl/EtOH conduce a disminuciones en el área superficial, atribuibles a la oclusión de los poros con material orgánico. La presencia de surfactante en las muestras fue determinada por FTIR. Ordered mesoporous silica was synthesized by the sol-gel process using tetraethoxysilane (TEOS) as silica source and hexadecyltrimethyl ammonium bromide (CTAB) as structure directing agent. Post-synthesis surfactant removal was conducted by two techniques: calcination, with progressive increases in temperature up to 550 ºC and solvent extraction using HCl /EtOH as extracting solution. In the last mentioned technique, a few experimental variables were changed such as the acid concentration, the volume of extracting solution, the reflux time and the solvent employed for washing. The samples were characterized by N2 adsorption, FTIR spectroscopy and SEM. Both the synthesis technique used and the procedures to remove template lead to MCM-41 type material. Template extraction by calcination results in materials having a surface area of 1100 m2 /g. On the other hand, extraction with HCl/EtOH leads to decreases in surface area, attributed to occlusion of the pores with organic material. In both cases, monitoring surfactant traces in the samples was performed using FTIR. Fil: Serrano, Melisa Romina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Salta. Instituto de Investigaciones para la Industria Química. Universidad Nacional de Salta. Facultad de Ingeniería. Instituto de Investigaciones para la Industria Química; Argentina Fil: Gramaglia Saracho, Agustina María Pía. Universidad Nacional de Salta. Facultad de Ingeniería. Escuela de Ingeniería Química; Argentina Fil: Acosta, Delicia Ester. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Salta. Instituto de Investigaciones para la Industria Química. Universidad Nacional de Salta. Facultad de Ingeniería. Instituto de Investigaciones para la Industria Química; Argentina Fil: Bonini, Norberto Alejandro. Universidad Nacional de Salta. Facultad de Ciencias Exactas; Argentina Fil: Gonzo, Elio Emilio. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Salta. Instituto de Investigaciones para la Industria Química. Universidad Nacional de Salta. Facultad de Ingeniería. Instituto de Investigaciones para la Industria Química; Argentina Fil: Parentis, Monica Liliana. Universidad Nacional de Salta. Facultad de Ingeniería; Argentina |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|