Effect of protective coating on microleakage of conventional glass ionomer cement and resin-modified glass ionomer cement in primary molars: An In vitro study
| Autor: | C Vishnurekha, Arthilakshmi, Ditto Sharmin, Parisa Norouzi Baghkomeh, Sankar Annamalai |
|---|---|
| Rok vydání: | 2018 |
| Předmět: |
Dye penetration
Molar Materials science 0206 medical engineering Glass ionomer cement microleakage Dentistry 02 engineering and technology In Vitro Techniques engineering.material Coating Humans In vitro study Tooth Deciduous General Dentistry Dental Leakage G-Coat Plus business.industry Resin modified General Medicine 021001 nanoscience & nanotechnology 020601 biomedical engineering Conventional glass ionomer cement lcsh:RK1-715 Resins Synthetic Glass Ionomer Cements lcsh:Dentistry engineering resin-modified glass ionomer cement 0210 nano-technology business primary molars |
| Zdroj: | Indian Journal of Dental Research, Vol 29, Iss 6, Pp 744-748 (2018) |
| ISSN: | 0970-9290 |
| DOI: | 10.4103/ijdr.ijdr_490_17 |
| Popis: | Aim: The aim of this in vitro study was to evaluate and compare the effect of protective coating G-Coat Plus on microleakage of conventional glass ionomer cement (CGIC) and resin-modified glass ionomer cement (RMGIC) in primary molars. Materials and Methods: A total of 120 samples were divided into four groups with 30 samples in each group. Group A – teeth restored with CGIC. Group B – teeth restored with CGIC coated with G-Coat Plus. Group C – teeth restored with RMGIC. Group D – teeth restored with RMGIC coated with G-Coat Plus. Microleakage was tested using 2% basic fuschin dye penetration and measured at ×40 original magnification under the stereomicroscope. Results: The results of this in vitro study showed that coating with G-Coat Plus showed a reduction in microleakage in CGIC and complete absence of microleakage in RMGIC when compared to the noncoated groups, which was statistically significant. CGIC without G-Coat Plus showed highest microleakage followed by RMGIC without G-Coat Plus, followed by a relatively less microleakage in CGIC with G-Coat Plus. Conclusion: Significant reduction in microleakage was seen in conventional GIC and RMGIC with G-Coat Plus when compared to conventional GIC and RMGIC without G-Coat Plus. |