Hormigón de altas resistencia reforzado con fibras de vidrio resistentes a alcalis en ambientes agresivos simulados
| Autor: | Chee Ban Cheah, K. Y. Chang, Mahyuddin Ramli, Wai Hoe Kwan |
|---|---|
| Rok vydání: | 2018 |
| Předmět: |
Materials science
Scanning electron microscope Glass fiber Fibre reinforcement 0211 other engineering and technologies 02 engineering and technology Chloride Refuerzo de fibra 021105 building & construction medicine lcsh:TA401-492 General Materials Science Scanning Electron Microscopy (SEM) Fiber Composite material Materials of engineering and construction. Mechanics of materials Microscopía electrónica de barrido (SEM) Vidrio Sulphate attack Ataque por sulfatos X-ray Diffraction (XRD) Building and Construction 021001 nanoscience & nanotechnology Durability Permeability (earth sciences) Mechanics of Materials TA401-492 Difracción de rayos X (XRD) Seawater lcsh:Materials of engineering and construction. Mechanics of materials Wetting Glass 0210 nano-technology medicine.drug |
| Zdroj: | Materiales de Construcción; Vol. 68 No. 329 (2018); e147 Materiales de Construcción; Vol. 68 Núm. 329 (2018); e147 Materiales de Construcción Consejo Superior de Investigaciones Científicas (CSIC) Materiales de Construccion, Vol 68, Iss 329, Pp e147-e147 (2018) |
| ISSN: | 1988-3226 0465-2746 |
| DOI: | 10.3989/mc.2018.v68.i329 |
| Popis: | The durability of the alkali-resistant (AR) glass fiber reinforced concrete (GFRC) in three simulated aggresive environments, namely tropical climate, cyclic air and seawater and seawater immersion was investigated. Durability examinations include chloride diffusion, gas permeability, X-ray diffraction (XRD) and scanning electron microscopy examination (SEM). The fiber content is in the range of 0.6 % to 2.4 %. Results reveal that the specimen containing highest AR glass fiber content suffered severe strength loss in seawater environment and relatively milder strength loss under cyclic conditions. The permeability property was found to be more inferior with the increase in the fiber content of the concrete. This suggests that the AR glass fiber is not suitable for use as the fiber reinforcement in concrete is exposed to seawater. However, in both the tropical climate and cyclic wetting and drying, the incorporation of AR glass fiber prevents a drastic increase in permeability. Este trabajo se centra en el estudio de la durabilidad de hormigón reforzado con fibra de vidrio resistente a álcalis (CRFVRA) en tres ambientes agresivos simulados como son, condiciones de clima tropical, ciclos de aire y agua de mar e inmersión marina. Los tests de durabilidad incluyeron la difusión de cloruros, permeabilidad de gas, difracción de rayos X (XRD) y evaluacion por microscopía electrónica de barrido (SEM). Los contenidos de fibra evaluados estuvieron en el rango desde 0.6% hasta 2.4%. Los resultados revelan que la muestra que contiene el mayor porcentaje de fibra sufre una severa pérdida de resistencia en condiciones de agua de mar, y una menor disminución de resistencia bajo condiciones cíclicas. Su permeabilidad disminuyó al incrementar el contenido de fibras en el hormigón. Lo anterior sugiere que el refuerzo con fibra resistente a alcalinos no es adecuado para su uso en hormigón en ambiente de agua de mar. Sin embargo, bajo condiciones de clima tropical, y en ciclos humedad/secado, la incorporación de dichas fibras previene un incremento drástico de la permeabilidad. |