La2Zr2O7 single buffer layer for YBCO RABiTS coated Conductors

Autor: Z. Saltyte, Michel Decroux, Carmen Jiménez, L. Porcar, Adulfas Abrutis, Patrick Chaudouët, François Weiss, T. Caroff, P. Odier, S. Morlens
Přispěvatelé: Laboratoire des matériaux et du génie physique (LMGP ), Institut National Polytechnique de Grenoble (INPG)-Institut polytechnique de Grenoble - Grenoble Institute of Technology (Grenoble INP )-Institut de Chimie du CNRS (INC)-Centre National de la Recherche Scientifique (CNRS), Consortium de Recherches pour l'Emergence des Technologies Avancées (CRETA), Centre National de la Recherche Scientifique (CNRS)-Université Grenoble Alpes [2016-2019] (UGA [2016-2019]), Department of General and Inorganic Chemistry [Vilnius], Vilnius University [Vilnius], Department of Condensed Matter Physics, University of Geneva [Switzerland], Thermodynamique et biophysique des petits systèmes (TPS), Institut Néel (NEEL), Université Joseph Fourier - Grenoble 1 (UJF)-Institut polytechnique de Grenoble - Grenoble Institute of Technology (Grenoble INP )-Centre National de la Recherche Scientifique (CNRS)-Université Joseph Fourier - Grenoble 1 (UJF)-Institut polytechnique de Grenoble - Grenoble Institute of Technology (Grenoble INP )-Centre National de la Recherche Scientifique (CNRS), Dpt of General and Inorganic Chemistry, Region Rhone Alpes Project SESUC, ANR-05-BLAN-0388,MADISUP(2005)
Jazyk: angličtina
Rok vydání: 2008
Předmět:
Zdroj: Superconductor Science and Technology
Superconductor Science and Technology, IOP Publishing, 2008, 21, pp.75007. ⟨10.1088/0953-2048/21/7/075007⟩
ISSN: 0953-2048
1361-6668
DOI: 10.1088/0953-2048/21/7/075007⟩
Popis: 8 pages; International audience; Chemical deposition methods like MOD and MOCVD are promising approaches for coated conductors (CCs) due to their reduced cost and easy scaling. High quality La2Zr2O7 (LZO) buffer layers were prepared by MOD on Ni-5%at.W (NiW) RABiTS and subsequent YBCO layers (450 to 800 nm thick) were deposited by pulsed injection MOCVD, leading to a simple low cost architecture NiWRABiTS/LZOMOD/YBCOMOCVD. In this novel combination of MOD and MOCVD approach, a single LZOMOD buffer layer is sufficient to ensure structural compatibility between YBCO and NiW, and protect the substrate from oxidation during YBCO MOCVD. YBCO films were epitaxially grown on LZO and exhibited critical current densities Jc close to 1 MA/cm2 at 77 K with a critical temperature Tc =91 K and DTc < 1 K.